Polyether amine modification of polypropylene

ABSTRACT

A compound comprising a blend of polypropylene with the reaction of a functionalized polypropylene and polyether amine in which the polyetheramine is grafted into the functionalized polypropylene in a customary mixing apparatus is disclosed. The blend may include an elastomer such as EP rubber and/or a filler such as glass. A process for producing the reaction product of the functionalized polypropylene and the polyether amine by melting with polypropylene in a customary mixing apparatus is also disclosed. Blends of the present invention are advantageously useful to prepare paintable automotive body parts.

This is a continuation-in-part of Ser. No. 08/499,521, filed Jul. 7, 1995, U.S. Pat. No. 5,783,630, which is a continuation-in-part application of Ser. No. 08/222,508, filed Apr. 4, 1994, now abandoned, which is a continuation application of Ser. No. 08/090,675, filed Jul. 13, 1993, now abandoned.

BACKGROUND OF THE INVENTION

This invention relates to a novel olefin polymer composed of the reaction of a functionalized polypropylene and a polyetheramine. This invention also relates to thermoplastic resin blends containing the novel olefin polymer and polypropylene.

The in situ formation of compatibilizers for polyblends is rapidly gaining popularity. In the last few years, more and more cases have been reported where advantage is taken of the presence of reactive groups to form a graft or a block or a random copolymer, which could act as a compatibilizer for a mixture of two or more polymers. The prior art, Process Requirements of the Reactive Compatibilization of Nylon 6/Polypropylene Blends by S. S. Dagli, M. Xanthos and J. A. Biensenberger: Polymer Processing Institute at Stevens Institute of Technology, Hoboken, N.J. 07030 reveals an acrylic acid grafted modified polypropylene used with a blend of nylon-6 and polypropylene.

Thermoplastic resin compositions containing polypropylene are well known in the art (e.g. U.S. Pat. No. 5,208,081). U.S. Pat. No. 5,179,164 describes a polypropylene/polyamide composition suitable for producing moldings. The patent describes an ethylene copolymer useful as an adhesion promoter. Moreover, the patent indicates that maleic acid is a suitable monomer for preparing the ethylene copolymer.

In addition, maleated polypropylene is commercially available.

European patent application 0 367 832 discloses a resin composition containing an olefinic polymer having acid anhydride groups. As in U.S. Pat. No. 5,179,164, the novel compound is blended with a polyamide.

Japanese patent 46003838 reveals a maleic anhydride modified polypropylene composition containing triethylamine and polyethylene glycol nonylphenyl ether. Japanese patent 60195120 reveals a molding containing polyethylene, maleic anhydride-grafted polyethylene, and diethylenetriamine.

However, the instant invention uses the maleic anhydride in conjunction with polyetheramines which produce unexpected improvements in resin properties.

SUMMARY OF THE INVENTION

This invention is a compound comprising a blend of polypropylene ("PP") with the reaction product of a functionalized polypropylene and polyetheramine in which the polyether amine is grafted onto the functionalized polypropylene in a customary mixing apparatus. By grafted it is meant that the amine functionality of the polyetheramine reacts with the anhydride component of the functionalized polypropylene to form a reaction product, for instance, a primary amine will react with a maleic anhydride to form an imide. This invention is also a process for producing the reaction product of the functionalized polypropylene and the polyether amine by melting with polypropylene in a customary mixing apparatus. In this regard, the compound blend of this invention may be prepared by reactive extrusion by feeding a polyetheramine, a functionalized polypropylene and polypropylene into an extruder at temperatures such that the polyetheramine reacts with the functionalized polypropylene to form a reaction product containing, for example, an imide group.

In another respect, this invention is a composition comprising polypropylene, a crosslinked thermoplastic polyolefin vulcanizate, and the reaction product of a functionalized polypropylene and a polyether amine.

The compositions of the present invention are useful for preparing molded automotive body parts, including directly paintable thermoplastic polyolefins ("TPO") based, and thermoplastic polyolefin vulcanizates ("TPV") based, automotive body parts.

It is also contemplated that the compositions are useful for making molded parts that contain filler such as glass. It is yet further contemplated that the compositions of the present invention may be useful in the preparation of films, including packaging films, to eliminate tie layers and to improve printability and barrier properties; fibers including dyable and non-woven PP fibers; and in packaging materials for electronics components such as semiconductor chips, wherein the packaging materials may provide electrostatic dissipation which would thereby protect the chips from damage. It is yet further contemplated that the composition of the present invention may be useful to improve the barrier properties for polyethylene and to modify polyethylene as a tie layer in multilayer films. It is further contemplated that the composition of the present invention may be useful as an additive as polypropylene based reinforcement fibers for concrete.

DESCRIPTION OF THE PREFERRED EMBODIMENT

The blend of polypropylene with the reaction product of maleated polypropylene and polyether amine shows improved paintability, improved impact resistance, and excellent mold flowability over blends of polypropylene and maleated polypropylene.

Plastics are increasingly being employed in the production of motor vehicles. Impact-modified PP has proved to be particularly suitable for applications such as bumpers, spoilers, fenders, side bump strips and the like. Therefore, a thermoplastic resin blend having the improved properties of the instant invention has significant potential commercial usefulness.

These resin compositions, according to the present invention, are useful as engineering plastics which are materials for structural members in the fields of transport machines (automobiles, ships and the like), apparatus, tools, electronic appliances, electric appliances, sporting goods, leisure goods and the like; and for connectors, tubes and the like.

Suitable polypropylenes are known from polymer chemistry, are described for example in Kunststoff-Handbuch, volume IV, Polyolefins, edited by R. Vieweg, A. Schley and A. Schwarz. Carol Hanser Verlag, Munich, 1969, and are commercially available, so that no details need be given.

Functionalized PP is PP onto which a monomer has been grafted. The usual method of such grafting is by free radical reaction. In the practice of this invention, the maleated polypropylene is not a copolymer of maleic anhydride or equivalent thereof, and propylene, such that the maleic anhydride moiety is predominantly in the backbone of the copolymer. Suitable monomers for preparing functionalized polypropylene are, for example, olefinically unsaturated monocarboxylic acids of less than 12 carbon atoms, e.g., acrylic acid or methacrylic acid, and the corresponding tert-butyl esters, e.g., tert-butyl (meth)acrylate, olefinically unsaturated dicarboxylic acids of less than 12 carbon atoms, e.g., fumaric acid, maleic acid, and itaconic acid and the corresponding mono-and/or di-tert-butyl esters, e.g., mono- or di-tert-butyl fumarate and mono- or di-tert-butyl maleate, olefinically unsaturated dicarboxylic anhydrides of less than 12 carbon atoms, e.g., maleic anhydride, sulfo- or sulfonyl-containing olefinically unsaturated monomers of less than 12 carbon atoms, e.g., p-styrenesulfonic acid, 2-(meth)acrylamide-2-methylpropenesulfonic acid or 2-sulfonyl(meth)acrylate, oxazolinyl-containing olefinically unsaturated monomers of less than 12 carbon atoms, e.g., vinyloxazolines and vinyloxazoline derivatives, and epoxy-containing olefinically unsaturated monomers of less than 12 carbon atoms, e.g., glycidyl (meth)acrylate or allyl glycidyl ether. The most preferred monomer for preparing functionalized polypropylene is maleic anhydride.

The functionalized polypropylene used in the practice of this invention may have a wide variety of number average molecular weights. When the functionalized polypropylene is used to make paintable articles, such as automotive body parts, the functionalized polypropylene preferably has a number average molecular weight greater than about 3,000 and preferably less than about 20,000, more preferably less than about 10,000. A representative example of a maleated polypropylene that is currently commercially available is under the name EPOLENE E-43, available from Eastman Chemical. Such relatively low molecular weight functionalized polypropylenes, when reacted with polyetheramines in accordance with the practice of this invention, appears to render the resulting extruded compositions more readily paintable. In other applications wherein the functionalized polypropylene is employed, such as when a glass filler is added to increase stiffness and strength, a higher average number molecular weight greater than about 20,000 may be employed.

Suitable anhydride functionalized polypropylene include the following structures: ##STR1## wherein PP is polypropylene. In these structures, it should be appreciated that the polypropylene can be bonded to one or two monomers when the polypropylene is linear, while more than two monomers might be included when the propylene is branched. Typically, one or two monomers are present.

Suitable polyetheramines include monamines, diamines and triamines, having a molecular weight of from about 150 to about 12,000. Preferred polyetheramines have a molecular weight of from about 1,000 to about 3,000. Suitable monamines include JEFFAMINE M-1000, JEFFAMINE M-2070, and JEFFAMINE M-2005. Suitable diamines include JEFFAMINE ED-6000, JEFFAMINE ED4000, JEFFAMINE ED-2001 including XTJ-502 and TXJ-418, JEFFAMINE D-2000, JEFFAMINE D4000, JEFFAMINE ED-900, JEFFAMINE ED-600, and JEFFAMINE D400. Suitable triamines include JEFFAMINE ET-3000, JEFFAMINE T-3000 and JEFFAMINE T-5000. Preferred polyetheramines include JEFFAMINE M-2070 and JEFFAMINE ED-2001. See the glossary for structures of these polyetheramines. More preferred polyetheramines of the present invention have a molecular weight in the range from about 1500 to about 2000. One especially preferred polyetheramine is a polyether monoamine which contains from about 36 to about 44 ethylene oxide units and from 1 to about 6 propylene oxide units. In one embodiment, such polyether monoamines have a molecular weight of about 2000 to about 2200. In another embodiment, the polyether monoamine contains about 40 to about 43 ethylene oxide units and from about 2.4 to about 3 propylene oxide units. Certain polyether monoamines are of formula: ##STR2## wherein m is about 36 to about 44 and wherein n is about 1 to about 6, including polyether monoamines wherein m is about 40 to about 43 and n is about 2.4 to about 3, as well as compounds of the formula having a molecular weight of about 2000 to about 2200.

In the practice of this invention, monoamines and diamines are preferred. Suitable polyether blocks for the polyetheramine include polyethylene glycol, polypropylene glycol, copolymers of polyethylene glycol and polypropylene glycol, poly(1,2-butylene glycol), and poly(tetramethylene glycol). The glycols can be aminated using well known methods to produce the polyetheramines. Generally, the glycols are prepared from ethylene oxide, propylene oxide or combination thereof using well known methods such as by a methoxy or hydroxy initiated reaction. When both ethylene oxide and propylene oxide are used, the oxides can be reacted simultaneously when a random polyether is desired, or reacted sequentially when a block polyether is desired.

In one embodiment of the present invention, the polyetheramines are prepared from ethylene oxide, propylene oxide or combinations thereof. Generally, when the polyetheramine is prepared from ethylene oxide, propylene oxide or combinations thereof, the amount of ethylene oxide on a molar basis is greater than about 50 percent of the polyetheramine, preferably greater than about 75 percent and more preferably greater than about 90 percent. In one embodiment of this invention, polyols and amines including polyalkylene polyamines and alkanol amines or any amine that is not a polyetheramine as disclosed herein may be absent from the composition. Similarly, functional groups other than ether linkages and amine groups may be absent from the polyetheramine. The polyether amines used in the practice of this invention can be prepared using well known amination techniques such as described in U.S. Pat. No. 3,654,370; U.S. Pat. No. 4,152,353; U.S. Pat. No. 4,618,717; U.S. Pat. No. 4,766,245; U.S. Pat. No. 4,960,942; U.S. Pat. No. 4,973,761; U.S. Pat. No. 5,003,107; U.S. Pat. No. 5,352,835; U.S. Pat. No. 5,422,042; and U.S. Pat. No. 5,457,147. Generally, the polyether amines are made by aminating a polyol, such as a polyether polyol with ammonia in the presence of a catalyst such as a nickel containing catalyst such as a Ni/Cu/Cr catalyst.

The mixing of the functionalized PP and polyetheramine and optionally also PP may be carried out in a customary mixing apparatus including batch mixers, continuous mixers, kneaders, and extruders. For most applications, the preferred mixing apparatus is an extruder.

Besides the PP/functionalized-PP/polyetheramine structural components according to the invention, the resin composition may, to improve the impact strength, contain impact modifiers, advantageously impact-modifying elastomers. Impact-modifying elastomers for the instant invention are known to a skilled worker. Examples are rubbers based on ethylene, propylene, butadiene, and acrylates, e.g. methacrylates, or mixtures thereof. Other examples include EP and EPDM rubbers, with EP rubber (ethylene propylene rubber) being preferred in applications where automotive body parts are being prepared. A representative example of a currently commercially available EP rubber is sold under the name VISTALON 878 by Exxon Chemical.

Suitable impact-modifying elastomers are described for example in Methoden der organischen Chemie (Houben-Weyl), volume XIV/1, Makromolekulare Chemie (Georg-Thieme-Verlag, Stuttgart, 1961), pages 390 to 406, and in the monograph by C. B. Bucknal, Toughened Plastics (Applied Publishers, London, 1977).

A composition containing polypropylene and elastomers, such as EP rubber, is commonly referred to as a "TPO," which stands for thermoplastic polyolefin. TPO's are commonly used in the manufacture of molded automotive body parts, such as bumper fascias. Such molded parts may also contain other components such as fillers, as described hereinbelow. TPO-based compositions can be prepared in the same manner as for non-elastomer-containing compositions. TPO's are commonly sold in compounded or reactor grades. Representative examples of TPO which are currently available commercially are described below in the paragraphs preceding Examples 18-27.

A composition containing polypropylene and vulcanized elastomers (vulcanized rubber), including thermoplastic polyolefin vulcanizates, is commonly referred to as a "TPV." TPV's are commonly used in the manufacture of molded automotive body parts, such as grips and handles. These molded parts may contain other components such as fillers, as described below. TPV-based compositions may be prepared in the same manner as for non-elastomer-containing compositions. A representative example of a commercially available TPV is described below with reference to Examples 28 and 29.

It is contemplated that the polyetheramine and functionalized polypropylene, and optionally a small amount of PP, TPV or TPO, can be reacted to form a reaction product concentrate and, later, the reaction product concentrate can be blended with polypropylene or TPO or TPV. In this aspect of the invention, the polyetheramine comprises from about 10 to about 50 weight percent of the concentrate. When the reaction product of polyether amine and maleated PP is prepared neat, the reaction product can be blended or compounded with polypropylene or TPO and any other components of the desired composition to the desired levels using a mixing apparatus such as an extruder. It should be understood that PP may be commonly used to dilute the reaction. Depending on the type of mixer, the reaction product, polypropylene and any other components can be thoroughly mixed as solids prior to introducing the admixture in the mixing apparatus. Alternatively, mixers are available which will mix the components during operation. In either case, during operation of the mixer, the components are heated to melt the solids, with the melted components being thereafter mixed to form the final composition.

In addition to the structural components of PP, functionalized-PP, and polyetheramine and any impact modifier contained in a resin composition according to the instant invention, the resin may also contain reinforcing agents and/or additives. The reinforcing agents used may be reinforcing fillers, for example, carbon or carbon fibers; clay, chalk, talc, and mica to control shrinkage and control coefficient of thermal expansion; glass (beads, fibers or mats such as of woven fibers) to increase stiffness. Further, the fillers may be finished with adhesion promoters and/or sizing agents. In addition, phosphite or hindered phenol or both can be added as a stabilizer (as a free radical scavenger).

When compositions include glass beads or fibers, the composition can contain up to about 40% glass filler if highly stiff compositions are desired. When compositions include glass mats, the composition can contain up to about 80% glass. More typically, from about 2% to about 10% glass filler in the composition is employed. Advantageously, the compositions of the present invention that contain glass filler generally are substantially free of voids that typically develop in compositions containing polypropylene and glass. While not wishing to be bound by theory, it is believed that the reaction product of polyether amine and maleated polypropylene serves to "wet" the glass to thereby make the glass and polypropylene more combinable (more miscible). In this aspect of the invention, it is preferred to employ maleated polypropylene having an average molecular weight of about 40,000 to about 60,000, as is described hereinabove. Generally, glass filler and polypropylene are not miscible, and their combination commonly leads to voids in the resulting compositions. The relatively higher molecular weight materials "wet" the glass to make the glass filler particles and polypropylene more combinable to thereby decrease the amount of voids in the resulting compositions.

The preferred functionalized polypropylene is a maleated polypropylene having the following structure: ##STR3## wherein PP is polypropylene.

The preferred polyetheramines are monoamines and diamines. The preferred monoamines as well as the preferred triamines have a molecular weight of from about 200 to about 4000. The preferred diamines have a molecular weight of from about 148 to about 6000. More preferred monoamines and diamines have a molecular weight of from about 1,000 to about 3,000.

In one embodiment, the preferred polyetheramine is a polyether monoamine which contains from about 36 to about 44 ethylene oxide units and from 1 to about 6 propylene oxide units. In one embodiment, such polyether monoamines have a molecular weight of from about 2000 to about 2200. In a particular embodiment, the polyether monoamine contains from about 40 to about 44 ethylene oxide units and about 2.4 to about 3 propylene oxide units. Such polyether monoamines may have the formula: ##STR4## wherein m is from about 36 to about 44, and wherein n is about 1 to about 6. Huntsman Corporation refers to one such polyether monoamine as XTJ418.

The preferred reaction product between the preferred functionalized polypropylene, maleated polypropylene, and the preferred polyetheramine has the following formula: ##STR5## wherein a is from about 5 to 50,000, for b:c from about 0:100 to 100:0, x is from about 1 to 3, and R is hydrogen or an alkyl moiety having a functionality of x (i.e., if x is 2, R is a divalent), the alkyl radical having 1 to 10 carbon atoms.

Suitable thermoplastic resin compositions may contain from about 66 to about 80 wt % TPO or TPV, from about 5 to about 30 wt % maleated PP and from about 2 to about 10 wt % polyetheramine. When the compositions include elastomers, such as in TPO-based compositions used to make automotive body parts, or TPV based compositions, the compositions generally comprise from about 5 to about 40 wt % maleated TPO or TPV, from about 2 to about 10 wt % polyetheramine and from about 50 to about 93 wt % PP, such percentages based on the weights of these components of the composition. Preferred compositions that include elastomers, or which are TPV-based, comprise about 15 to about 30 wt % maleated PP, from about 2 to about 8 wt % polyetheramine and from about 62 to about 83 wt % TPO or TPV.

The preferred customary mixing apparatus is an extruder in which the polyetheramine is grafted onto the maleated polypropylene at from about 175 to 300° C. in the course of a residence time of from about 25 to 300 seconds. For typical compositions of this invention, degradation begins to occur above this temperature range and below this range the compositions generally do not melt. Polypropylene is a non-reactive component of the mixing blend. The preferred temperature range is from about 190 to 260° C. Excess moisture in the blended composition may cause surface blemishes upon molding, but the moisture can be removed by the normal drying processes, including the use of heated, dry air.

Molded articles prepared from compositions according to the present invention are generally directly paintable. Representative examples of paints commonly employed for this purpose include urethane-based and melamine-based paints. Such paints may be applied using conventional techniques. Advantageously, compositions of the present invention may be painted directly without solvent borne chlorinated polyethylene pretreatment and optionally without primer, though a primer may be used.

In the examples, continuous compounding was carried out in a Werner & Pfleiderer 30 mm twin screw extruder (ZSK30), having a nine barrel configuration, three kneading zones and one vent section, in which the feed sequence was a combined feed in which all the components fed at the same location (hopper of the extruder).

The following examples which illustrate the nature of the instant invention are not intended to be limitative. In the examples, a stoichiometric excess of maleic functionality on the maleated polypropylene is used relative to the amount of amine functionality on the polyetheramine.

EXAMPLES 1-6

Blends of PP, maleated PP (MAL-PP), and JEFFAMINE M2070 produced in an extruder exhibit characteristics in percent compositions as shown in Table 1 in which the remaining percent is PP:

                  TABLE 1                                                          ______________________________________                                         Example  1       2       3     4     5     6                                   ______________________________________                                         % MAL-PP 20              30                                                    % M2070  0       2       4     0     2     4                                     FM, psi 284K 255K 226K 289K 256K 201K                                          StY, psi 8660 7980 7030 8750 7830 6170                                         TE, % 8 16 10 4 13 5                                                           TSt, psi 4990 4770 4280 5000 4630 3720                                         NI, ft lb/in 0.161 0.220 0.386 0.123 0.139 0.220                               UnI, ft lb/in 12 14 10 10 14 5                                               ______________________________________                                          where:                                                                         FM--flexural modulus                                                           StY--stress at yield                                                           TE--Tensile elongation                                                         TSt--tensile strength                                                          NI--notched izod impact                                                        UnI--unnotched izod impact                                               

EXAMPLES 7-10

Table 2 reveals the effects of JEFFAMINE M2070 (M) as compared to JEFFAMINE ED2001 (ED) in which either is blended with from about 76 to 78 wt % of PP, and from about 20 wt % of MAL-PP in an extruder.

                  TABLE 2                                                          ______________________________________                                         Example      7        8        9      10                                       ______________________________________                                         J. Type      M        ED       M      ED                                       % JEFF.      2             4                                                   FM, psi      255K     246K     226K   230K                                       StY, psi 7980 7730 7030 7140                                                   TE, % 16 10 10 16                                                              TSt, psi 4770 4560 4280 4420                                                   NI, ftlb/in 14 15 10 18                                                        UnI, ftlb/in 14 15 10 18                                                     ______________________________________                                          where:                                                                         FM  flexural modulus                                                           StY  stress at yield                                                           TE  Tensile elongation                                                         TSt  tensile strength                                                          NI  notched izod impact                                                        UnI  unnotched izod impact.                                              

EXAMPLES 11-17

Table 3 reveals the percent paint adhesion of various compositions of PP, maleated PP, and the JEFFAMINES indicated relative to an unmodified PP control sample wherein the blends were produced in an extruder.

                  TABLE 3                                                          ______________________________________                                         Ex-          MAL-                  Paint  Con-                                   ample PP PP % J. Type Adhesion trol                                          ______________________________________                                         11    76%    20%     4% JEFFAMINE M1000                                                                           62%    2%                                     12 76% 20% 4% JEFFAMINE ED-6000 28% 4%                                         13 74% 20% 6% JEFFAMINE ED-6000 46% 4%                                         14 74% 20% 6% JEFFAMINE ED-4000 40% 4%                                         15 74% 20% 6% JEFFAMINE-2070 77% 21%                                           16 72% 20% 8% JEFFAMINE-2070 40% 21%                                           17 72% 20% 8% JEFFAMINE-2001 68% 21%                                         ______________________________________                                    

In the following Examples 18-27, there are shown modified TPO-based (thermoplastic olefin-based) compositions including polyether amines of the present invention (in Tables 18A, 19A, 20A, 21A, 22A, 23A, 24A, 25A, 26A, and 27A), the physical properties of the compositions (in Tables 18B, 19B, 20B, 21B, 22B, 23B, 24B, 25B, 26B, and 27B) and the paint adhesion of the compositions (in Tables 18C, 19C, 20C, 21C, 22C, 23C, 24C, 25C, 26C, and 27C). Examples 28-29 show TPV-based compositions. In the Tables shown in Examples 18-29, the following phrases have the indicated meanings:

"HIMONT CA53A" is a reactor grade TPO containing polypropylene ("PP") and ethylene propylene rubber ("EP rubber") obtained from Himont, which may be described as having medium melt flow.

"Phenol" is ETHANOX 330 which is a hindered phenol stabilizer obtained from Albemarle.

"EPOLENE E43" is a maleated PP obtained from Eastman Chemical, having about 4 wt % maleation as determined from proton nmr.

"HIMONT LB150161" is a reactor grade TPO having a high melt flow.

"AMOCO 1016" is a PP having a melt flow rate at 230° C. of about 5 g/min. as indicated by the supplier, Amoco Chemical.

"DEXFLEX D-161" is a compounded TPO of PP and EP rubber which is described as having medium melt flow by the supplier, D&S Plastics International.

"NICHIBAN" refers to the tradename of a tape obtained from a Japanese company.

"STAMYLAN P" is an impact EP copolymer containing 5-10% ethylene in the backbone obtained from DSM having a melt flow at 230° C./2.16 Kg using an 150 R1133 procedure of 4.7 dg/min. as reported by the supplier, Dutch State Mines ("DSM").

"KELTAN TP-0552-2" is a TPO having a melt flow of 6.5 at 230° C./2.16 Kg using an ISO R1133 procedure of 6.5 dg/min. as reported by the supplier, DSM.

"VISTALON 878" is an EP rubber available from Exxon Chemical.

"WIIPA" means with isopropanol wipe prior to painting and "W/O IPA" means without isopropanol wipe painting.

In Examples 18-29, the sample compositions were injection molded to prepare type I tensile bars, which were used in the adhesion tests. The following procedures were used in these examples.

A hand mixed blend of polypropylene, maleated polypropylene, polyether amine and an antioxidant is produced and added to the feed hopper. The extruder heater bands are set to the following profile: feed throat 200° C., 220° C., 220° C., 220° C., 220° C., 220° C. die face.

The blend is fed into the feed throat of a Werner Pfleiderer ZSK30 twin screw extruder. The compounded product is cooled in a water bath and pelletized.

Test specimens were injection molded using an ENGEL 55 ton injection molding machine using the following conditions:

    ______________________________________                                         Heating Zones:                                                                            Next to                                                                            Nozzle   Nozzle Feed Zone                                                                              Feed Zone                               ______________________________________                                                    199° C.                                                                          196° C.                                                                          196° C.                                                                         196° C.                              Mold Temperature 27° C.                                               ______________________________________                                    

Physical test specimens were allowed to equilibrate at 24° C. and at 50% relative humidity for 48 hours. Tensile measurements were made according to ASTM D638 on an INSTRON frame using a crosshead speed of 10 cm/min. Flexural properties were measured according to ASTM D790 using a crosshead speed of 1.25 cm/min. Izod impact properties were measured according to ASTM D256.

Dynamical mechanical spectrometry (DMS) was performed using a RHEOMETRICS RDS-II. Injection molded bars measuring 12 mm×50 mm×3 mm were tested in rectangular torsion mode at 1 hz. Strains imposed upon the samples were typically between 0.05% and 0.2%. Measurements were shown to be strain insensitive over the region investigated. The storage and the loss moduli as well as tan delta were measuring from -120° C. up through the melting of the samples, using a heating rate of 2° C./min. in a nitrogen atmosphere. Samples were tested after conditioning at 24° C. and 50% relative humidity for 24 hours.

Paint adhesion testing involved painting four inch injection molded discs with a white, two component urethane automotive paint supplied by RED SPOT PAINTS. The paint is applied with a high volume, low pressure BINKS spray gun. The painted disks are based for 30 minutes at 80° C. The specimens are conditioned 24 hours and then tested using a crosshatch/tape adhesion test where a multibladed scribe is used to generate 100 squares (approximately 2 mm×2 mm per square) on the disks. A piece of tape (Scotch Brand 2040, 3M) is then applied over the squares and then the tape is pulled from the disk. The percentages denoted in the tables reflect the number of painted squares remaining after pulling the tape from the disk.

EXAMPLE 18

                  TABLE 18A                                                        ______________________________________                                                                 JEFFAMINE ®                                          Sample TPO.sup.1 MAL-PP.sup.2 M-2070 Phenol PP                               ______________________________________                                         1      99.7%   --       --        0.3%                                           2 84.7% -- -- 0.3% 15%                                                         3 79.7%  -- 0.3% 20%                                                           4 84.7% 15% -- 0.3%                                                            5 79.7% 20% -- 0.3%                                                            6 80.7% 15% 4% 0.3%                                                            7 78.7% 15% 6% 0.3%                                                            8 75.7% 20% 4% 0.3%                                                            9 73.7% 20% 6% 0.3%                                                            10 71.7% 20% 8% 0.3%                                                           11 80.7% 15% 4% 0.3%                                                           12 78.7% 15% 6% 0.3%                                                           13 75.7% 20% 4% 0.3%                                                           14 73.7% 20% 6% 0.3%                                                           15 71.7% 20% 8% 0.3%                                                         ______________________________________                                          .sup.1 HIMONT CA53A                                                            .sup.2 EPOLENE E43                                                       

                  TABLE 18B                                                        ______________________________________                                                        1       2      3     4    5                                     ______________________________________                                           Flexural Modulus, MPa 578 725 736 686 741                                      Stress at Yield, MPa 19.1 23.3 24.1 22.6 24.4                                  Tensile Elongation, % 667 666 622 559 417                                      Tensile Strength, MPa 16.2 18.9 18.8 16.1 16.7                                 Young's Modulus, MPa 338 432 453 423 452                                       Notched Izod Impact, J/m 554 493 382 100 72.9                                  -30° C., J/m 55.0 49.4 43.3 44.3 34.0                                   Unnotched Izod Impact, J/m 839 1025 931 924 997                                Falling Dart Impact                                                            Max Load, J/m 1430 1624 1652 1556 1485                                         Total E, J 21.6 23.7 25.6 23.1 16.0                                            DSC                                                                            Tm, °C. 156 156 158 153 164                                             Delta H, J/g 61.8 63.5 72.0 9.7 78.2                                           Tc, °C. 98.9 103 104 102 109                                            Delta H, J/g 69.5 79.1 80.8 74.8 81.6                                           6 7 8 9 10                                                                  ______________________________________                                           Flexural Modulus, MPa 643 560                                                  Stress at Yield, MPa 21.1 17.3                                                 Tensile Elongation, % 296 53                                                   Tensile Strength, MPa 15.3 13.2                                                Young's Modulus, MPa 390 364                                                   Notched Izod Impact, J/m 154 363                                               -30° C., J/m 33.2 33.7                                                  Unnotched Izod Impact, J/m 828 651                                             Falling Dart Impact                                                            Max Load, J/m 1406 1064 1247 1043 905                                          Total E, J 19.1 11.4 15.9 11.0 9.59                                            DSC                                                                            Tm, °C. 152  151 150 150                                                Delta H, J/g 61.6  62.4 63.7 63.3                                              Tc, °C. 101  102 103 103                                                Delta H, J/g 73.7  73.3 73.2 72.8                                               11 12 13 14 15                                                              ______________________________________                                           Flexural Modulus, MPa 586 572 579 596 648                                      Stress at Yield, MPa 18.2 17.4 18.5 18.8 19.8                                  Tensile Elongation, % 666 666 666 666 666                                      Tensile Strength, MPa 14.8 14.9 13.3 13.7 14.7                                 Young's Modulus, MPa 348 322 323 342 342                                       Hardness Shore D 57 56 57 57 56                                                Notched Izod Impact, J/m 563 574 116 184 565                                   -30° C., J/m 40.9 34.9 34.4 27.0 29.0                                   Unnotched Izod Impact, J/m 840 780 847 772 756                                 Falling Dart Impact                                                            Max Load, J/m 1541 1523 1505 1557 1539                                         Total E, J 22.8 23.0 20.7 21.9 23.0                                          ______________________________________                                    

                  TABLE 18Ci                                                       ______________________________________                                         ADHESION TEST                                                                          % Adhesion             % Adhesion                                              Test   Test   Test         Test Test Test                                SAMPLE 1 2 3 SAMPLE 1 2 3                                                    ______________________________________                                         PP       0      0          PP       0    2                                       1  0  2  1  0  0                                                               2 19 32  2  0  1                                                               3  5  1  3  1  5                                                               4 49 23 36 4  0  0                                                             5 61 57 59 5  0  0                                                             6 80 99 90 6 65 52 58                                                          7 100  78 89 7 26  5 16                                                        8 77 62 70 8 43 30 36                                                          9 91 90 90 9 90 98 94                                                          10  93 98 96 10  82 91  6                                                          11  80 94 87                                                             ______________________________________                                    

                  TABLE 18Cii                                                      ______________________________________                                         CROSS-HATCH ADHESION TEST                                                                         S1                                                            (SAMPLE) W/IPA                                                               ______________________________________                                                6       100%                                                              7 100%                                                                         9 100%                                                                         10 96%                                                                         11 100%                                                                        14 100%                                                                      ______________________________________                                    

                  TABLE 18Ciii                                                     ______________________________________                                         CROSS-HATCH ADHESION TEST                                                                         S1       S2                                                   (SAMPLE) W/O IPA W/O IPA                                                     ______________________________________                                         11             97       100                                                      12 0 4                                                                         13 82 88                                                                       14 95 98                                                                       15 7 9                                                                       ______________________________________                                    

EXAMPLE 19

                  TABLE 19A                                                        ______________________________________                                                                    JEFFAMINE ®                                       Sample TPO.sup.1 MAL-PP.sup.2 M-2070 Phenol                                  ______________________________________                                         1      99.7%     --        --         0.3%                                       2 84.7% 15% -- 0.3%                                                            3 79.7% 20% -- 0.3%                                                            4 69.7% 30% -- 0.3%                                                            5 80.7% 15% 4% 0.3%.                                                           6 78.7% 15% 6% 0.3%                                                            7 75.7% 20% 4% 0.3%                                                            8 73.7% 20% 6% 0.3%                                                            9 71.7% 20% 8% 0.3%                                                            10 65.7% 30% 4% 0.3%                                                           11 63.7% 30% 6% 0.3%                                                           12 61.7% 30% 8% 0.3%                                                           13 80.7% 15% 4% 0.3%                                                           14 78.7% 15% 6% 0.3%                                                           15 75.7% 20% 4% 0.3%                                                           16 73.7% 20% 6% 0.3%                                                           17 71.7% 20% 8% 0.3%                                                           18 65.7% 30% 4% 0.3%                                                           19 63.7% 30% 6% 0.3%                                                           20 61.7% 30% 8% 0.3%                                                         ______________________________________                                          .sup.1 HIMONT CA53A                                                            .sup.2 EPOLENE E43                                                       

                  TABLE 19B                                                        ______________________________________                                                        1       2      3     4    5                                     ______________________________________                                           Flexural Modulus,MPa 1234 1314 1329 1379 1351                                  Stress at Yield, MPa 39.1 41.6 42.5 43.9 39.9                                  Tensile Elongation, % 186 59 18 10 159                                         Tensile Strength, MPa 25.3 25.9 26.4 26.5 25.1                                 Young's Modulus, MPa 694 732 789 809 715                                       Notched Izod Impact, J/m 69.3 47.0 43.3 25.2 57.2                              -30° C., J/m 33.5 19.1 17.7 16.5 18.8                                   Unnotched Izod Impact, J/m 1413 1095 965 694 945                               Falling Dart Impact                                                            Max Load, J/m 2096 2148 1010 344 1137                                          Total E, J 30.9 29.8 4.69 1.46 5.70                                            DSC                                                                            Tm, °C. 166 165  164 165                                                Delta H, J/g 86.6 85.8  95.2 94.2                                              Tc, °C. 109 109  110 109                                                Delta H, J/g 106 105  104 99.3                                                          6       7       8    9     10   11                                  ______________________________________                                           Flexural Modulus, 1128 1253 1108 1017 1280 1186                                MPa                                                                            Stress at Yield, 31.6 37 28.4 23 35.4 31.4                                     MPa                                                                            Tensile 11 19 8.8 8.3 8.3 6.9                                                  Elongation, %                                                                  Tensile 20.8 24.1 20 17.6 22.8 20.4                                            Strength, MPa                                                                  Young's Modulus, 661 708 677 624 742 701                                       MPa                                                                            Notched Izod 72.5 50.4 47.1 42.2 26.6 17.7                                     Impact, J/m                                                                    -30° C., J/m 15.2 11.7 10.2 9.5 7.5 6.6                                 Unnotched Izod 262 475 178 172 241 191                                         Impact, J/m                                                                    Falling Dart Impact                                                            Max Load, J/m 630 356 329 368 219 220                                          Total E, J 3.53 1.63 2.66 2.37 1.2 1.23                                        DSC                                                                            Tm, °C. 165 165 166 164 164 164                                         Delta H, J/g 93.9 97.3 95.7 91.4 97.7 93.5                                     Tc, °C. 109 109 110 109 110 108                                         Delta H, J/g 98 101 7.1 96 101 97.3                                          ______________________________________                                    

                  TABLE 19C                                                        ______________________________________                                         ADHESION TEST                                                                  ______________________________________                                         % Adhesion                 % Adhesion                                                  Test   Test   Test         Test Test Test                                SAMPLE 1 2 3 SAMPLE 1 2 3                                                    ______________________________________                                         PP.sup.1                                                                                0      0          PP       0    2                                       1  0  2   1  0  0                                                              2 19 32   2  0  1                                                              3  5  1   3  1  5                                                              4 49 23 36  4  0  0                                                            5 61 57    0  0                                                                6 80 99 90  6 65 52 58                                                         7 100  78 89  7 26  5 16                                                       8 77 62 70  8 43 30 36                                                         9 91 90 90  9 90 98 94                                                         10  93 98 96 10  82 91  6                                                          11  80 94 87                                                             ______________________________________                                         % Adhesion                 % Adhesion                                          Sample                                                                               Test 1     Test 2  Sample Test                                                                            1     Test 2                                  ______________________________________                                           13  0%  0% 13  0%  0%                                                          14  0%  0% 14  0%  6%                                                          15  1%  0% 15 20%  1%                                                          16  0% 11% 16  4% 36%                                                          17  0%  0% 17  0%  3%                                                          18 28% 17% 18 23% 26%                                                          19 22% 13% 19 13% 11%                                                          20 89% 62% 20 27% 21%                                                        ______________________________________                                          .sup.1 Control                                                           

EXAMPLE 20

                  TABLE 20A                                                        ______________________________________                                                                 JEFFAMINE ®                                                                          EP                                             Sample PP.sup.1 MAL-PP.sup.2 M-2070 RUBBER.sup.3 Phenol                      ______________________________________                                         1     74.7%    5%       --        20%                                            2 69.7% 10% -- 20% 0.3%                                                        3 59.7% 15% -- 25% 0.3%                                                        4 70.7% 5% 4% 20% 0.3%                                                         5 68.7% 5% 6% 20% 0.3%                                                         6 66.7% 5% 8% 20% 0.3%                                                         7 65.7% 10% 4% 20% 0.3%                                                        8 63.7% 10% 6% 20% 0.3%                                                        9 61.7% 10% 8% 20% 0.3%                                                        10 55.7% 15% 4% 25% 0.3%                                                       11 53.7% 15% 6% 25% 0.3%                                                       12 51.7% 15% 8% 25% 0.3%                                                     ______________________________________                                          .sup.1 AMOCO 1016                                                              .sup.2 EPOLENE E43                                                             .sup.3 VISTALON                                                          

                  TABLE 20B                                                        ______________________________________                                                         1       2       3     4                                        ______________________________________                                           Flexural Modulus, MPa 1342 1411 1333 1359                                      Stress at Yield, MPa 38.6 40.2 36.5 36.4                                       Tensile Elongation, % 168 140 173 451                                          Tensile Strength, MPa 25.2 25.4 22.7 22.5                                      Young's Modulus, MPa 731 750 699 671                                           Hardness, Shore D 66 69 64 67                                                  Notched Izod Impact, J/m 108 59 107 338                                        -30° C., J/m 17.6 16.6 18.0 23.1                                        Unnotched Izod Impact, J/m 1106 1199 1311 1252                                 Falling Dart Impact                                                            Maximum Load, J/m 2045 2035 1826 1879                                          -30° C., J/m 3417 3351 3122 2888                                        Total Energy, J 30.0 29.2 26.2 25.9                                            -30° C., J 41.9 34.6 39.4 22.2                                           5 6 7 8                                                                     ______________________________________                                           Flexural Modulus, MPa 1070 1029 1168 1064                                      Stress at Yield, MPa 29.6 28.0 31.6 28.3                                       Tensile Elongation, % 125 106 188 119                                          Tensile Strength, MPa 19.1 18.1 19.9 18.2                                      Young's Modulus, MPa 575 552 595 555                                           Hardness, Shore D 63 61 64 63                                                  Notched Izod Impact, J/m 361 444 273 286                                       -30° C., J/m 28.4 43.8 19.2 18.4                                        Unnotched Izod Impact, J/m 867 816 874 785                                     Falling Dart Impact                                                            Maximum Load, J/m 1710 1495 1858 1338                                          -30° C., J/m 920 595 2101 385                                           Total Energy, J 18.5 14.8 22.8 13.5                                            -30° C., J 30.5 2.19 12.4 1.58                                           9 10 11 12                                                                  ______________________________________                                           Flexural Modulus, MPa 1006 178 968 915                                         Stress at Yield, MPa 26.4 28.8 26.4 24.0                                       Tensile Elongation, % 122 196 184 40                                           Tensile Strength, MPa 17.1 18.2 17.2 15.6                                      Young's Modulus, MPa 523 553 527 500                                           Hardness, Shore D 61 62 61 60                                                  Notched Izod Impact, J/m 256 277 240 127                                       -30° C., J/m 24.0 25.0 26.4 13.8                                        Unnotched Izod Impact, J/m 729 904 860 782                                     Falling Dart Impact                                                            Maximum Load, J/m 1024 1606 1317 1110                                          -30° C., J/m 339 1021 500 561                                           Total Energy, J 9.2 18.9 13.5 9.9                                              -30° C., J 1.74 4.31 2.50 2.69                                        ______________________________________                                    

                  TABLE 20C                                                        ______________________________________                                         CROSS-HATCH ADHESION TEST                                                                    S1      S2      S1     S2                                          SAMPLE W/IPA W/IPA W/O IPA W/O IPA                                           ______________________________________                                         1         19%     20%       0%     2%                                            2 19% 44% 11% 13%                                                              3 50% 89% 99% 100%                                                             4 40% 59% 37% 52%                                                              5 29% 55% 5% 33%                                                               6 92% 100% 4% 39%                                                              7 82% 89% 28% 32%                                                              8 95% 100% 68% 100%                                                            9 97% 78% 70% 75%                                                              1 83% 100% 99% 100%                                                            11 99% 100% 82% 96%                                                            12 92% 100% 100% 100%                                                        ______________________________________                                    

EXAMPLE 21

                  TABLE 21A                                                        ______________________________________                                                                    JEFFAMINE ®                                       Sample TPO.sup.1 MAL-PP.sup.2 M-2070 Phenol                                  ______________________________________                                         1      100%      --        -          0.3%                                       2 90% 10% -- 0.3%                                                              3 85% 15% -- 0.3%                                                              4 80% 20% -- --                                                                5 85.8% 10% 4% 0.2%                                                            6 83.8% 10% 6% 0.2%                                                            7 80.8% 15% 4% 0.2%                                                            8 78.8% 15% 6% 0.2%                                                            9 75.8% 20% 4% 0.2%                                                            10 73.8% 20% 6% 0.2%                                                           11 80.8% 15% 4% 0.2%                                                           12 78.8% 15% 6% 0.2%                                                           13 75.8% 20% 4% 0.2%                                                           14 73.8% 20% 6% 0.2%                                                         ______________________________________                                          .sup.1 DEXFLEX D161                                                            .sup.2 EPOLENE E43                                                       

                  TABLE 21B                                                        ______________________________________                                                        1       2      3     4    5                                     ______________________________________                                           Flexural Modulus, MPa 944 985 1050 1101 857                                    Stress at Yield, MPa 25.1 27.4 29.3 30.7 23.9                                  Tensile Elongation, % 506 186 116 78 466                                       Tensile Strength, MPa 17.8 18.7 19.5 20.1 16.8                                 Young's Modulus, MPa 551 581 629 654 491                                       Hardness Shore D 63 65 67 68 63                                                Notched Izod Impact, J/m 576 343 84 54 475                                     -30° C., J/m 35.9 31.5 25.1 16.9 33.6                                   Unnotched Izod Impact, J/m 1027 965 1174 1066 944                              Falling Dart Impact                                                            Max Load, J/m 1669 1678 1703 1721 1509                                         -30° C., J/m 2980 3140 3094 2880 2397                                   Total E, J 24.1 22.8 22.7 21.8 21.9                                            -30° C., J 36.9 38.0 29.7 17.0 28.8                                      6 7 8 9 10                                                                  ______________________________________                                           Flexural Modulus, MPa 748 832 745 788 804                                      Stress at Yield, MPa 20.8 23.0 20.4 22.6 22.4                                  Tensile Elongation, % 71 100 31 26 18                                          Tensile Strength, MPa 14.7 16.1 14.5 16.3 15.0                                 Young's Modulus, MPa 445 486 451 492 460                                       Hardness Shore D 61 64 451 61 60                                               Notched Izod Impact, J/m 331 252 60 74 56                                      -30° C., J/m 37.8 22.2 144 17.2 18.3                                    Unnotched Izod Impact, J/m 736 737 22.7 419 310                                Falling Dart Impact                                                            Max Load, J/m 1340 1408 1047 1047 704                                          -30° C., J/m 550 422 356 411 339                                        Total E, J 15.1 15.7 9.0 7.4 5.1                                               -30° C., J 1.31 0.82 0.62 0.70 0.53                                                   11      12      13    14                                       ______________________________________                                           Flexural Modulus, MPa 892 802 945 874                                          Stress at yield, MPa 26.2 23.7 27.1 25.4                                       Tensile Elongation, % 221 511 187 370                                          Tensile Strength, MPa 18.1 16.8 18.3 17.4                                      Young's Modulus, MPa 525 467 539 495                                           Hardness Shore D 63 63 64 61                                                   Notched Izod Impact, J/m 159 511 99 118                                        -30° C., J/m 26.6 25.9 20.6 18.7                                        Unnotched Izod Impact, J/m 1020 934 1174 913                                   Falling Dart Impact                                                            Max Load, J/m 1610 1603 1591 1618                                              -30° C., J/m 2655 1541 1517 1259                                        Total E, J 22.4 23.6 19.1 19.5                                                 -30° C., J 20.8 5.45 6.24 4.88                                        ______________________________________                                    

                  TABLE 21C                                                        ______________________________________                                         CROSS-HATCH ADHESION TEST                                                                     S1      S2      S1     S2                                         (SAMPLE) W/IPA W/IPA W/O IPA W/O IPA                                         ______________________________________                                         PP.sup.1   0.00    0.00      0.00                                                1 3 18 78 27                                                                   2 63 63 94 48                                                                  3 79 59 62 100                                                                 4 0.00 14 87 83                                                                5 100 100 100 100                                                              6 100 100 100 100                                                              7 100 100 99 100                                                               8 100 100 97 100                                                               9 100 100 100 100                                                              10 100 100 100 100                                                             11 67 67 94 88                                                                 12 62 62 10 22                                                                 13 100 100 100 100                                                             14 100 100 100 100                                                           ______________________________________                                          .sup.1 Control.                                                          

EXAMPLE 22

                  TABLE 22A                                                        ______________________________________                                                                    JEFFAMINE ®                                       Sample TPO.sup.1 MAL-PP.sup.2 M-2070 Phenol                                  ______________________________________                                         1      100%      --        --         --                                         2 90% 10% -- --                                                                3 85% 15% -- --                                                                4 80% 20% -- --                                                                5 85.8% 10% 4% 0.2%                                                            6 83.8% 10% 6% 0.2%                                                            7 80.8% 15% 4% 0.2%                                                            8 78.8% 15% 6% 0.2%                                                            9 75.8% 20% 4% 0.2%                                                            10 73.8% 20% 6% 0.2%                                                           11 80.8% 15% 4% 0.2%                                                           12 78.8% 15% 6% 0.2%                                                           13 75.8% 20% 4% 0.2%                                                           14 73.8% 20% 6% 0.2%                                                         ______________________________________                                          .sup.1 STAMYLAN P                                                              .sup.2 EPOLENE E43                                                       

                  TABLE 22B                                                        ______________________________________                                                     1      2      3    4    5    6    7                                ______________________________________                                           Flexural Modulus, 1053 1123 1185 1259 1100 1025 1040                           MPa                                                                            Stress at Yield, MPa 32.3 35.3 36.5 38.9 32.7 30.0 31.0                        Tensile Elongation, % 453 173 141 36 168 30 22                                 Tensile Strength, MPa 21.2 22.7 23.1 23.7 21.5 19.9 20.3                       Young's Modulus, 568 647 665 696 581 571 592                                   MPa                                                                            Notched Izod Impact, 716 607 159 118 519 482 219                               J/m                                                                            -30° C., J/m 77.4 43.5 34.7 23.5 37.0 47.8 33.5                         Unnotched Izod 1075 1246 1078 1124 911 853 629                                 Impact, J/m                                                                    Falling Dart Impact                                                            Max Load, J/m 1987 2002 2013 2052 1853 1614 1632                               -30° C., J/m 3562 3721 2804 1154 1464 461 503                           Total Energy, J 31.4 31.1 30.0 28.8 25.9 17.4 18.1                             -30° C., J 45.2 42.7 17.2 3.6 5.3 0.9 1.0                             ______________________________________                                            8 9 10 11 12 13 14                                                          ______________________________________                                           Flexural Modulus, 995 1062 999 1107 1083 1131 1076                             MPa                                                                            Stress at Yield, MPa 26.9 30.8 28.4 33.9 32.2 34.0 32.5                        Tensile Elongation, % 14 15 11 218 483 80 230                                  Tensile Strength, MPa 18.3 19.9 18.5 21.4 20.1 21.7 20.8                       Young's Modulus, 542 582 560 587 517 619 582                                   MPa                                                                            Notched Izod Impact, 238 109 104 495 563 145 157                               J/m                                                                            -30° C., J/m 34.6 24.2 22.7 27.1 39.8 28.5 26.8                         Unnotched Izod 514 464 336 1029 1008 1004 863                                  Impact, J/m                                                                    Falling Dart Impact                                                            Max Load, J/m 1301 1003 1021 2017 2002 941 1878                                -30° C., J/m 460 455  3633 1244 1140 1193                               Total Energy, J 11.0 8.3 6.3 30.2 29.5 7.9 26.4                                -30° C., J 0.7 0.7  26.8 3.6 3.2 3.5                                  ______________________________________                                    

                  TABLE 22C                                                        ______________________________________                                         CROSS-HATCH ADHESION TEST                                                        DISC SAMPLE S1       S2     S1      S2                                         TAPE 3M.sup.1 3M NICHIBAN NICHIBAN                                             SAMPLE W/IPA W/IPA W/O IPA W/O IPA                                           ______________________________________                                         1         6%       0%       0%      3%                                           2 1% 0% 14% 1%                                                                 3 1% 0% 7% 2%                                                                  4 0% 6% 1% 15%                                                                 5 45% 80% 83% 32%                                                              6 96% 98% 96% 100%                                                             7 88% 96% 82% 92%                                                              8 89% 78% 74% 96%                                                              9 94% 87% 100% 98%                                                             10 99% 100% 100% 100%                                                          11 3% 47% 20% 27%                                                              12 7% 1% 2% 3%                                                                 13 38% 79% 35% 78%                                                             14 85% 65% 100% 97%                                                          ______________________________________                                          .sup.1 Scotch Brand 2040                                                 

                  TABLE 22C                                                        ______________________________________                                         CROSS-HATCH ADHESION TEST                                                        DISC SAMPLE  S1       S2     S1      S2                                        SAMPLE W/IPA W/IPA W/O IPA W/O IPA                                           ______________________________________                                         1          4%       1%       5%      0%                                          2 0% 0% 7% 0%                                                                  3 4% 0% 4% 10%                                                                 4 9% 1% 17% 1%                                                                 5 26% 79% 57% 46%                                                              6 95% 90% 93% 92%                                                              7 95% 89% 94% 89%                                                              8 83% 84% 97% 97%                                                              9 85% 94% 98% 96%                                                              10 96% 88% 99% 97%                                                             11 83% 58% 90% 71%                                                             12 0% 5% 8% 20%                                                                13 86% 95% 74% 92%                                                             14 97% 86% 92% 98%                                                             15.sup.1 98% 98% 100% 100%                                                   ______________________________________                                          .sup.1 Reactive extrusion product of 73% STAMYLAN P, 20% EPOLENE E43, 6%       Jeffamine ® M2070, and 0.2% Phenol.                                  

EXAMPLE 23

                  TABLE 23A                                                        ______________________________________                                                                 JEFFAMINE ®                                                                          EP                                             Sample PP.sup.1 MAL-PP.sup.2 M-2070 RUBBER.sup.3 Phenol                      ______________________________________                                         1     69.7%    --       --        30%    0.3%                                    2 59.7% 10% -- 30% 0.3%                                                        3 56.7% 13% -- 30% 0.3%                                                        4 52.2% 17.5% -- 30% 0.3%                                                      5 57.7% 10% 2% 30% 0.3%                                                        6 55.7% 10% 4% 30% 0.3%                                                        7 53.7% 10% 6% 30% 0.3%                                                        8 54.7% 13% 2% 30% 0.3%                                                        9 52.7% 13% 4% 30% 0.3%                                                        10 50.7% 13% 6% 30% 0.3%                                                       11 50.2% 17.5% 2% 30% 0.3%                                                     12 48.2% 17.5% 4% 30% 0.3%                                                     13 46.2% 17.5% 6% 30% 0.3%                                                     14 57.7% 10% 2% 30% 0.3%                                                       15 55.7% 10% 4% 30% 0.3%                                                       16 53.7% 10% 6% 30% 0.3%                                                       17 54.7% 13% 2% 30% 0.3%                                                       18 52.7% 13% 4% 30% 0.3%                                                       19 50.7% 13% 6% 30% 0.3%                                                       20 50.2% 17.5% 2% 30% 0.3%                                                     21 48.2% 17.5% 4% 30% 0.3%                                                     22 46.2% 17.5% 6% 30% 0.3%                                                   ______________________________________                                          .sup.1 AMOCO 1016                                                              .sup.2 EPOLENE E43                                                             .sup.3 VISTALON 878                                                      

                  TABLE 23B                                                        ______________________________________                                                  1      2      3    4    5    6    7    8                              ______________________________________                                           Flexural 1064 1095 1166 1156 1062 843 741 959                                  Modulus, MPa                                                                   Stress at 28.5 29.7 32.5 31.3 27.4 22.8 20.1 25.7                              Yield, MPa                                                                     Tensile 483 211 181 151 252 356 107 316                                        Elongation, %                                                                  Tensile 19.5 19.7 20.2 19.2 18.1 15.2 13.7 16.6                                Strength, MPa                                                                  Young's 583 608 608 611 551 456 412 487                                        Modulus, MPa                                                                   Hardness, 64 63 65 64 61 60 59 59                                              Shore D                                                                        Notched Izod 576 436 252 161 510 449 450 427                                   Impact, J/m                                                                    -30° C., 58.4 28.0 22.2 26.0 33.0 54.3 54.9 31.4                        J/m                                                                            Unnotched 979 957 976 867 955 847 815 819                                      Izod Impact,                                                                   J/m                                                                            Falling Dart                                                                   Impact                                                                         Max Load, J/m 1711 1760 1710 1607 1565 1431 1199 1514                          -30° C., J/m 3096 3236 3245 3177 3014 1487 802 2962                     Total Energy, J 25.5 29.2 22.5 20.6 27.3 18.1 14.2 20.0                        -30° C., J 39.1 41.5 42.6 37.4 40.1 6.8 3.6 19.6                        Ductile/5 5 5 5 5 5 5 5 5                                                      -30° C./5 5 5 5 3 5 0 0 0                                             ______________________________________                                            9 10 11 12 13 14 15 16                                                      ______________________________________                                           Flexural 798 746 863 792 709 991 964 907                                       Modulus, MPa                                                                   Stress at 22.2 20.3 23.9 21.8 19.5 26.8 25.4 23.6                              Yield, MPa                                                                     Tensile 157 65 252 94 33 498 494 656                                           Elongation, %                                                                  Tensile 15.0 13.7 16.3 14.9 13.6 18.1 17.3 17.5                                Strength, MPa                                                                  Young's 437 387 476 436 408 503 479 437                                        Modulus, MPa                                                                   Hardness, 61 59 61 60 60 62 59 58                                              Shore D                                                                        Notched Izod 439 384 258 271 205 530 575 586                                   Impact, J/m                                                                    -30° C., 40.9 31.0 25.5 28.6 29.8 49.8 33.9 56.1                        J/m                                                                            Unnotched 818 679 712 778 665 1146 1108 1012                                   Izod Impact,                                                                   J/m                                                                            Falling Dart                                                                   Impact, J/m                                                                    Max Load, J/m 1370 1224 1452 1258 1027 1649 1631 1554                          -30° C., J/m 1224 718 1229 580 487 3098 3096 3060                       Total Energy, J 16.1 14.6 18.6 13.9 11.9 24.0 23.6 23.8                        -30° C., J 5.0 3.4 5.8 2.6 3.4 40.0 40.1 39.8                           Ductile/5 5 5 5 5 5 5 5 5                                                      -30° C./5 0 0 0 0 0 5 5 5                                             ______________________________________                                                  17      18      19    20    21    22                                  ______________________________________                                           Flexural 986 946 921 964 922 889                                               Modulus, MPa                                                                   Stress at 27.2 25.0 23.5 26.4 24.8 23.0                                        Yield, MPa                                                                     Tensile 511 578 605 87 109 202                                                 Elongation, %                                                                  Tensile 1.67 16.0 15.7 17.7 16.7 16.2                                          Strength, MPa                                                                  Young's 456 439 404 518 477 475                                                Modulus, MPa                                                                   Hardness, 62 60 58 62 62 54                                                    Shore D                                                                        Notched Izod 463 549 594 209 357 551                                           Impact, J/m                                                                    -30° C., J/m 27.7 30.9 34.1 19.9 30.2 24.7                              Unnotched 996 922 804 899 1011 774                                             Izod Impact,                                                                   J/m                                                                            Falling Dart                                                                   Impact                                                                         Max Load, J/m 1541 1602 1534 1484 1429 1418                                    -30° C., J/m 3199 3171 3131 2932 3215 3225                              Total Energy, J 20.9 22.8 22.2 18.2 18.4 20.6                                  -30° C., J 41.6 41.9 41.4 24.4 40.6 41.8                                Ductile/5 5 5 5 5 5 5                                                          -30° C./5 5 5 5 1 5 5                                                 ______________________________________                                    

                  TABLE 23C                                                        ______________________________________                                         CROSS-HATCH ADHESION TEST                                                                     S1      S2      S1     S2                                         (SAMPLE) W/IPA W/IPA W/O IPA W/O IPA                                         ______________________________________                                         PP.sup.1   0%                0%                                                  1 94% 72% 35% 1%                                                               2 74% 57% 73% 45%                                                              3 10% 25% 26% 36%                                                              4 80% 62% 16% 24%                                                              5 94% 97% 54% 94%                                                              6 99% 100% 94% 97%                                                             7 100% 100% 100% 100%                                                          8 100% 100% 100% 100%                                                          9 100% 100% 100% 100%                                                          10 100% 100% 100% 100%                                                         11 100% 100% 97% 100%                                                          12 100% 100% 100% 100%                                                         13 97% 95% 98% 100%                                                            14 94% 100% 69% 79%                                                            15 65% 59% 0% 0%                                                               16 39% 52% 0% 0%                                                               17 100% 100% 67% 71%                                                           18 85% 88% 8% 2%                                                               19 75% 43% 20% 3%                                                              20 100% 100% 99% 100%                                                          21 100% 100% 93% 100%                                                          22 83% 78% 2% 2%                                                             ______________________________________                                          .sup.1 Control                                                           

EXAMPLE 24

                  TABLE 24A                                                        ______________________________________                                                                    JEFFAMINE ®                                       Sample TPO.sup.1 MAL-PP.sup.2 M-2070 Phenol                                  ______________________________________                                         1      100%      --        --         --                                         2 90% 10% -- --                                                                3 85% 15% -- --                                                                4 80% 20% -- --                                                                5 85.8% 10% 4% 0.2%                                                            6 83.8% 10% 6% 0.2%                                                            7 80.8% 15% 4% 0.2%                                                            8 78.8% 15% 6% 0.2%                                                            9 75.8% 20% 4% 0.2%                                                            10 73.8% 20% 6% 0.2%                                                           11 80.8% 15% 4% 0.2%                                                           12 78.8% 15% 6% 0.2%                                                           13 75.8% 20% 4% 0.2%                                                           14 73.8% 20% 6% 0.2%                                                         ______________________________________                                          .sup.1 KELTAN TP 05522                                                         .sup.2 EPOLENE E43                                                       

                  TABLE 24B                                                        ______________________________________                                                     1      2      3    4    5    6    7                                ______________________________________                                           Flexural Modulus, 915 971 1034 1076 799 724 780                                MPa                                                                            Stress at Yield, MPa 23.1 25.5 27.6 28.4 21.5 18.4 21.1                        Tensile Elongation, % 529 61 36 16 38 20 17                                    Tensile Strength, MPa 15.6 16.1 16.6 17.0 14.8 13.4 14.8                       Young's Modulus, 504 534 570 588 459 432 461                                   MPa                                                                            Hardness, Shore D 61 61 63 64 58 56 58                                         Notched Izod Impact, 669 551 160 111 486 402 413                               J/m                                                                            -30° C., J/m 700 101 71.3 56.7 96.4 75.6 70.6                           Unnotched Izod 944 877 942 937 810 706 805                                     Impact, J/m                                                                    Falling Dart Impact                                                            Max Load, J/m 1695 1732 1399 1747 1522 1178 1453                               -30° C., J/m 2912 3013 3110 2932 1389 529 839                           Total Energy, J 27.8 26.9 21.0 22.2 19.0 14.4 17.8                             -30° C., J 40.5 40.6 29.9 18.6 5.4 4.2 4.3                              Ductile/5 5 5 5 5 5 5 5                                                        -30° C./5 5 5 1 0 0 0 0                                               ______________________________________                                            8 9 10 11 12 13 14                                                          ______________________________________                                           Flexural Modulus, 718 812 760 863 798 871 845                                  MPa                                                                            Stress at Yield, MPa 19.0 21.7 19.9 22.8 21.6 23.4 22.9                        Tensile Elongation, % 12 11 11 82 478 65 92                                    Tensile Strength, MPa 13.7 15.0 13.9 15.7 15.6 16.3 16.1                       Young's Modulus, 441 487 462 473 463 486 478                                   MPa                                                                            Hardness, Shore D 56 59 58 62 59 61 61                                         Notched Izod Impact, 438 128 200 519 620 147 166                               J/m                                                                            -30° C., J/m 42.3 38.4 29.1 61.7 44.1 50.8 37.7                         Unnotched Izod 570 574 374 850 855 905 828                                     Impact, J/m                                                                    Falling Dart Impact                                                            Max Load, J/m 1155 1284 924 1544 1579 1516 1544                                -30° C., J/m 454 545 487 2989 2300 2287 1526                            Total Energy, J 13.2 10.7 6.7 19.9 24.4 16.3 21.1                              -30° C., J 3.4 2.9 3.6 22.3 12.0 10.8 10.4                              Ductile/5 5 0 0 5 5 0 5                                                        -30° C./5 0 0 0 0 0 0 0                                               ______________________________________                                    

                  TABLE 24C                                                        ______________________________________                                         CROSS-HATCH ADHESION TEST                                                                     S1      S2      S1     S2                                         (SAMPLE) W/IPA W/IPA W/O IPA W/O IPA                                         ______________________________________                                         PP.sup.1   0%                0%                                                  1 96% 88%. 86% 90%                                                             2 72% 75% 53% 24%                                                              3 69% 41% 43% 10%                                                              4 41% 15% 40% 3%                                                               5 100% 100% 100% 100%                                                          6 100% 100% 100% 100%                                                          7 100% 100% 100% 100%                                                          8 100% 100% 100% 100%                                                          9 100% 100% 100% 100%                                                          10 100% 100% 99% 100%                                                          11 100% 100% 100% 100%                                                         12 98% 100% 78% 3%                                                             13 100% 88% 100% 100%                                                          14 100% 100% 100% 100%                                                         15.sup.2 100% 100%                                                           ______________________________________                                          .sup.1 Control                                                                 .sup.2 Reactive extrusion product of 73% STAMYLAN P, 20% EPOLENE E43, 6%       Jeffamine ® M2070, and 0.2% Phenol.                                  

EXAMPLE 25

                  TABLE 25A                                                        ______________________________________                                                         MAL-            EP                                               Sample PP.sup.1 PP.sup.2 AMINE.sup.3 RUBBER.sup.4 Phenol                     ______________________________________                                         1      74.7%    5%       --     20%     0.3%                                     2 69.7% 10% -- 20% 0.3%                                                        3 59.7% 15% -- 25% 0.3%                                                        4 70.7% 5% 4% 20% 0.3%                                                         5 68.7% 5% 6% 20% 0.3%                                                         6 66.7% 5% 8% 20% 0.3%                                                         7 65.7% 10% 4% 20% 0.3%                                                        8 63.7% 10% 6% 20% 0.3%                                                        9 61.7% 10% 8% 20% 0.3%                                                        10 55.7% 15% 4% 25% 0.3%                                                       11 53.7% 15% 6% 25% 0.3%                                                       12 51.7% 15% 8% 25% 0.3%                                                     ______________________________________                                          .sup.1 AMOCO 1016                                                              .sup.2 EPOLENE E43                                                             .sup.3 A polyether monoamine containing 40 ethylene oxide units and 2.4        propylene oxide units, generally of the formula shown in the Glossary for      JEFFAMINE ® M2070, which is referred to within Huntsman Corporation a      "XTJA18.                                                                       .sup.4 VISTALON 878                                                      

                  TABLE 25B                                                        ______________________________________                                                        1      2      3    4    5    6                                  ______________________________________                                           Flexural Modulus, MPa 1233 1218 1134 1197 1098 994                             Stress at Yield, MPa 35.1 35.2 31.7 33.0 30.9 28.6                             Tensile Elongation, % 189 182 148 159 262 116                                  Tensile Strength, MPa 23.7 23.6 21.3 22.0 20.3 18.4                            Young's Modulus, MPa 642 648 612 618 580 527                                   Hardness, Shore D 64 65 63 65 63 62                                            Notched Izod Impact, J/m 128 82 100 282 451 470                                -30° C., J/m 15.2 16.2 17.2 16.0 15.6 23.1                              Unnotched Izod Impact, J/m 1056 1237 1144 1091 969 981                         Falling Dart Impact                                                            Max Load, J/m 1915 1848 1728 1788 1753 1408                                    -30° C., J/m 3480 3496 3325 2495 2191 479                               Total Energy, J 27.0 25.2 22.2 22.9 22.5 14.2                                  -30° C., J 43.5 40.0 42.2 20.4 9.6 2.0                                  Ductile/5 5 5 5 5 5 5                                                          -30° C./5 5 4 5 2 0 0                                                 ______________________________________                                            7 8 9 10 11 12                                                              ______________________________________                                           Flexural Modulus, MPa 1161 1029 970 976 922 910                                Stress at Yield, MPa 32.1 29.2 28.5 26.8 25.6 25.3                             Tensile Elongation, % 374 240 118 376 474 185                                  Tensile Strength, MPa 20.5 18.9 18.3 17.7 16.0 17.0                            Young's Modulus, MPa 570 552 521 505 469 486                                   Hardness, Shore D 64 61 60 61 60 60                                            Notched Izod Impact, J/m 366 383 315 391 425 341                               -30° C., J/m 17.9 16.8 19.2 20.2 19.8 17.6                              Unnotched Izod Impact, J/m 893 781 854 857 799 827                             Falling Dart Impact                                                            Max Load, J/m 1787 1449 1046 1546 1252 995                                     -30° C., J/m 3079 588 542 1668 676 492                                  Total Energy, J 23.5 14.8 10.2 18.4 13.2 10.0                                  -30° C., J 20.8 2.6 2.6 7.0 2.6 2.2                                     Ductile/5 5 5 5 5 5 5                                                          -30° C./5 0 0 0 0 0 0                                                 ______________________________________                                    

                  TABLE 25C                                                        ______________________________________                                         CROSS-HATCH ADHESION TEST                                                        DISC                                                                           SAMPLE S1  S2 S1 S2                                                            TAPE 3M.sup.1  3M NICHIBAN NICHIBAN                                            SAMPLE W/O IPA  W/O IPA W/O IPA W/O IPA                                      ______________________________________                                         PP.sup.2                                                                              0%                      1%                                                1 8% 4% 1% 12% 49%                                                             2 1% 2% 4% 39% 43%                                                             3 87% 90% 91% 97% 100%                                                         4 49% 53% 57% 87% 95%                                                          5 98% 98% 97% 100% 100%                                                        6 99% 100% 100% 100% 100%                                                      7 100% 100% 99% 100% 100%                                                      8 98% 99% 100% 100% 100%                                                       9 100% 100% 100% 100% 100%                                                     10 100%  100% 100% 100%                                                        11 190%  100% 100% 100%                                                        12 100%  100% 100% 100%                                                      ______________________________________                                          .sup.1 Scotch Brand 2040                                                       .sup.2 Control                                                           

EXAMPLE 26

                  TABLE 26A                                                        ______________________________________                                                                    JEFFAMINE ®                                       Sample TPO.sup.1 MAL-PP.sup.2 M-2070 Phenol                                  ______________________________________                                         1      100%      --        --         --                                         2 90% 10% -- --                                                                3 85% 15% -- --                                                                4 80% 20% -- --                                                                5 85.8% 10% 4% 0.2%                                                            6 83.8% 10% 6% 0.2%                                                            7 80.8% 15% 4% 0.2%                                                            8 78.8% 15% 6% 0.2%                                                            9 75.8% 20% 4% 0.2%                                                            10 73.8% 20% 6% 0.2%                                                           11 80.8% 15% 4% 0.2%                                                           12 78.8% 15% 6% 0.2%                                                           13 75.8% 20% 4% 0.2%                                                           14 73.8% 20% 6% 0.2%                                                         ______________________________________                                          .sup.1 KELTAN TP 2632                                                          .sup.2 EPOLENE E43                                                       

                  TABLE 26B                                                        ______________________________________                                                     1      2      3    4    5    6    7                                ______________________________________                                           Flexural Modulus, 1648 1838 1863 1895 1537 1314 1415                           MPa                                                                            Stress at Yield, MPa 26.9 32.7 33.9 34.2 27.5 23.8 25.7                        Tensile Elongation, % 93 6 4 2 9 9 6                                           Tensile Strength, MPa 15.9 18.7 19.0 18.9 17.0 15.4 15.9                       Young's Modulus, 876 1007 1065 1080 881 779 802                                MPa                                                                            Hardness, Shore D 63 64 64 64 62 57 60                                         Notched Izod Impact, 518 56 98 23 126 204 63                                   J/m                                                                            -30° C., J/m 146 36 24 14 27 32 19                                      Unnotched Izod 1147 923 691 327 920 508 417                                    Impact, J/m                                                                    Falling Dart Impact                                                            Max Load, J/m 1496 1644 1628 1222 1408 1044 916                                -30° C., J/m 2499 2662 2371 799 1040 597 566                            Total Energy, J 22.0 21.1 20.1 9.72 16.7 10.1 8.45                             -30° C., J 34.7 21.6 13.1 5.14 3.61 3.15 2.96                           Ductile/5 5 5 5 0 3 5 0                                                        -30° C./5 5 0 0 0 0 0 0                                               ______________________________________                                            8 9 10 11 12 13 14                                                          ______________________________________                                           Flexural Modulus, 1285 1439 1261 1356 1173 1479 1323                           MPa                                                                            Stress at Yield, MPa 22.8 25.8 22.6 27.6 26.1 28.7 27.0                        Tensile Elongation, % 6 4 5 8 10 4 6                                           Tensile Strength, MPa 15.0 16.4 14.9 17.7 17.4 17.4 17.0                       Young's Modulus, 767 887 777 738 663 862 743                                   MPa                                                                            Hardness, Shore D 59 60 60 62 60 61 59                                         Notched Izod Impact, 58 27 31 55 92 32 40                                      J/m                                                                            -30° C., J/m 16 13 12 22 22 15 18                                       Unnotched Izod 313 334 222 691 812 632 771                                     Impact, J/m                                                                    Falling Dart Impact                                                            Max Load, J/m 719 492 334 1548 1555 929 1207                                   -30° C., J/m 518 487 472 1923 1161 616 812                              Total Energy, J 5.92 4.02 2.71 18.9 19.0 7.08 10.8                             -30° C., J 3.07 2.63 2.82 7.76 5.34 3.85 4.02                           Ductile/5 0 0 0 4 5 0 0                                                        -30° C./5 0 0 0 0 0 0 0                                               ______________________________________                                    

                  TABLE 26C                                                        ______________________________________                                         CROSS-HATCH ADHESION TEST                                                        DISC SAMPLE  S1      S2     S1      S2                                         TAPE 3M.sup.1 3M NICHIBAN NICHIBAN                                             SAMPLE W/IPA W/IPA W/O IPA W/O IPA                                           ______________________________________                                         PP.sup.2    0%               0%                                                  1  77%  84%  65%  92%                                                          2  32%  0%  22%  5%                                                            3  1%  4%  8%  8%                                                              4  0%  0%  7%  13%                                                             5 100% 100%  99%  96%                                                          6 100% 100% 100% 100%                                                          7 100% 100%  95%  82%                                                          8 100% 100%  88% 100%                                                          9  99%  98% 100% 100%                                                          10  100% 100% 100% 100%                                                        11  100%  96% 100%  93%                                                        12   74%  19%  57%  77%                                                        13   83%  62% 100%  64%                                                        14   91%  84%  91%  93%                                                      ______________________________________                                          .sup.1 Scotch Brand 2040                                                       .sup.2 Control                                                           

EXAMPLE 27

                  TABLE 27A                                                        ______________________________________                                         Sample TPO.sup.1                                                                               MAL-PP.sup.2                                                                             AMINE.sup.3                                                                            Phenol PP.sup.4                              ______________________________________                                         1      99.7%    --        --      0.3%                                           2 84.7% -- -- 0.3% 15%                                                         3 79.7% -- -- 0.3% 20%                                                         4 89:7% 10% -- 0.3%                                                            5 84.7% 10% -- 0.3%                                                            6 79.7% 20% -- 0.3%                                                            7 85.7% 10% 4% 0.3%                                                            8 83.7% 10% 6% 0.3%                                                            9 80.7% 15% 4% 0.3%                                                            10 78.7% 15% 6% 0.3%                                                           11 75.7% 20% 4% 0.3%                                                           12 73.7% 20% 6% 0.3%                                                           13 71.7% 20% 8% 0.3%                                                         ______________________________________                                          .sup.1 HIMONT CA53A                                                            .sup.3 A polyether monoamine containing 40 ethylene oxide units and 2.4        propylene oxide units, generally of the formula shown in the Glossary for      JEFFAMINE ® M2070, which is referred to within Huntsman Corporation a      "XTJ418.                                                                       .sup.4 AMOCO 1016                                                              .sup.2 EPOLENE E43                                                       

                  TABLE 27B                                                        ______________________________________                                                     1      2      3    4    5    6    7                                ______________________________________                                           Flexural Modulus, 510 646 705 588 664 734 546                                  MPa                                                                            Stress at Yield, MPa 15.8 19.8 21.4 18.7 20.6 22.7 17.2                        Tensile Elongation, % 666 666 666 666 666 484 531                              Tensile Strength, MPa 14.6 17.0 18.1 14.6 14.6 15.5 12.3                       Young's Modulus, 284 368 394 340 375 414 310                                   MPa                                                                            Hardness, Shore D 58 60 60 59 61 62 57                                         Notched Izod Impact, 589 582 597 529 398 94 499                                J/m                                                                            -30° C., J/m 65 47 38 38 37 37 40                                       Unnotched Izod 722 867 841 727 882 958 704                                     Impact, J/m                                                                    Falling Dart Impact                                                            Max Load, J/m 1428 1589 1632 1486 1513 1529 1334                               -30° C., J/m 3007 3335 3506 3290 3278 2610 889                          Total Energy, J 20.6 22.6 23.4 20.9 20.6 21.1 16.0                             -30° C., J 39.4 39.3 44.6 43.0 38.5 18.0 3.7                            Ductile/5 5 5 5 5 5 5 5                                                        -30° C./5 5 4 5 5 4 0 0                                               ______________________________________                                                        8      9      10   11   12   13                                 ______________________________________                                           Flexural Modulus, MPa 502 529 618 603 591 653                                  Stress at Yield, MPa 16.4 16.9 18.6 18.8 18.5 19.6                             Tensile Elongation, % 208 245 170 138 37 43                                    Tensile Strength, MPa 11.7 12.2 13.0 13.5 13.5 13.8                            Young's Modulus, MPa 299 309 355 348 354 381                                   Hardness, Shore D 52 58 57 52 57 59                                            Notched Izod Impact, J/m 443 437 445 310 162 90                                -30° C., J/m 46 35 36 28 25 22                                          Unnotched Izod Impact, 601 642 834 871 732 789                                 J/m                                                                            Falling Dart Impact                                                            Max Load, J/m 1180 1255 1207 1263 1205 908                                     -30° C., J/m 760 2344 1505 1018 911 688                                 Total Energy, J 12.9 14.1 14.2 14.4 13.2 7.0                                   -30° C., J 3.2 12 6.3 3.3 3.1 3.1                                       Ductile/5 5 5 5 5 5 0                                                          -30° C./5 0 0 0 0 0 0                                                 ______________________________________                                    

                  TABLE 27C                                                        ______________________________________                                         CROSS-HATCH ADHESION TEST                                                        DISC SAMPLE S1       S2      S1      S2                                        TAPE 3M.sup.1 3M NICHIBAN NICHIBAN                                             SAMPLE W/O IPA W/O IPA W/O IPA W/O IPA                                       ______________________________________                                         PP.sup.2  5%                 2%                                                  1 29% 67% 74% 92%                                                              2 66% 76% 81% 84%                                                              3 61% 73% 78% 61%                                                              4 100% 98% 100% 98%                                                            5 96% 100% 100% 99%                                                            6 85% 94% 91% 96%                                                              7 100% 100% 100% 100%                                                          8 100% 100% 100% 100%                                                          9 100% 100% 100% 100%                                                          10 100% 100% 100% 100%                                                         11 100% 100% 100% 100%                                                         12 100% 100% 100% 100%                                                         13 100% 100% 100% 100%                                                       ______________________________________                                          .sup.1 Scotch Brand 2040                                                       .sup.2 Control                                                           

Examples 18-27 demonstrate that TPO modified with the reaction product of maleated PP and polyether amines of this invention provides a composition that is directly paintable. This paintability is surprising and unexpected in that the TPO's used to make automotive body parts, such as bumper fascias, are not directly readily paintable to a commercially acceptable level. Heretofore, in order to render automotive TPO based molded body parts paintable, the parts were treated with an adhesion promoter comprised of low molecular weight chlorinated polyethylene and a solvent, which results in a toxic waste stream that must be properly disposed of, and which adds to the cost of the parts. Alternatively, the parts could be heat treated using plasma irradiation, or otherwise partially burning the surface of the parts. This procedure is also expensive and may be, moreover, prone to variability in result owing to batch to batch variances from procedure and errors by the operator.

Compositions prepared in accordance with the practice of the present invention generally may be directly painted, with or without a primer, such that the paint adhesion is greater than about 75 percent based on the testing procedure described above for Examples 18-27, preferably greater than about 85 percent, more preferably greater than about 90 percent, and most preferably greater than about 95 percent.

Compositions prepared in accordance with the present invention may be used to prepare molded articles of manufacture using conventional, well known, molding techniques under standard conditions. For instance, standard injection molding techniques can be employed. Certain compositions (blends) of the present invention have surprisingly been found to have improved flowability characteristics during injection molding of TPO-based compositions such that less pressure may be used when injecting the melted compositions into a mold, as compared to compositions in which polyetheramine is absent. The desired shape of the molded article may vary depending on end use of the article. For instance, rubber containing compositions of the present invention may be injection molded to manufacture automotive body parts such as bumper fascias.

In the following Examples 28-29, there are shown modified TPV-based (thermoplastic polyolefin vulcanizate-based) compositions that include polyether amines of the present invention (Tables 28A and 29A), and the physical properties of the compositions (Tables 28B and 29B, including paint adhesion). In Examples 28-29, and Tables 28A, 28B, 29A, and 29B, the TPV employed was SANTOPRENE 101-87, available from Advance Elastomer Systems. SANTOPRENE 101-87 is believed to contain PP and dynamically vulcanized rubber. In Example 28, the amine employed was the same polyether amine used in Table 27A as described in footnote 3.

                  TABLE 28A                                                        ______________________________________                                                         EPOLENE                                                          Sample TPV E-43 AMINE EHTANOX 330                                            ______________________________________                                         1      100%     --         --      --                                            2 89.8% 10% -- 0.2%                                                            3 85.8% 10% 4% 0.2%                                                            4 83.8% 10% 6% 0.2%                                                            5 80.8% 15% 4% 0.2%                                                            6 78.8% 15% 6% 0.2%                                                            7 75.8% 20% 4% 0.2%                                                            8 73.8% 20% 6% 0.2%                                                            9 71.8% 20% 8% 0.2%                                                          ______________________________________                                    

EXAMPLE 28

                                      TABLE 28B                                    __________________________________________________________________________                 1  2  3  4  5  6  7  8  9                                          __________________________________________________________________________     Flexural Modulus, MPa                                                                      196                                                                               294                                                                               252                                                                               272                                                                               282                                                                               316                                                                               321                                                                               345                                                                               366                                          Stress at Yield, MPa 7.1 9.5 8.5 8.8 9.1 9.8 10.2 10.8 10.8                    Tensile Elongation, % 666 666 666 666 644 666 479 467 118                      Tensile Strength, MPa 12.0 12.3 11.6 11.6 11.4 11.4 10.4 10.4 7.9                                                 Hardness Shore D 41 45 43 44 45 47                                            47 48 49                                     Notched Izod Impact, J/m 268 388 380 357 402 377 354 198 120                   -30° C., J/m 606 114 103 81 58 49 25 30 19                              Falling Dart Impact                                                            Max Load, J/m 824 915 854 836 870 865 878 892 813                              -30° C., J/m 1529 1749 1827 1655 1570 1597 1042 1194 782                                                   Total E, J 19.4 20.2 18.9 18.5 17.7                                           18.4 15.5 16.2 8.7                           -30° C., J 26.2 25.9 22.0 20.6 9.0 11.1 4.5 5.8 3.0                     Ductile/5 5 5 5 5 5 5 5 5 5                                                    -30° C., J 5 5 5 5 0 0 0 0 0                                            MFI, gm/10 min. 0.3 4.0 5.1 23 40 47 63 90 154                                 Paint Adhesion w/IPA, % 30 49 72 100 72 92 92 96 100                           w/o IPA, % 46 23 70 100 66 72 69 78 100                                      __________________________________________________________________________

EXAMPLE 29

                  TABLE 29A                                                        ______________________________________                                                         EPOLENE   JEFFAMINE ®                                                                          ETHANOX                                      Sample TPV E-43 M-2070 330                                                   ______________________________________                                         1      100%     --        --        --                                           2 89.8% 10% -- 0.2%                                                            3 84.8% 15% -- 0.2%                                                            4 79.8% 20% -- 0.2%                                                            5 85.8% 10% 4% 0.2%                                                            6 83.8% 10% 6% 0.2%                                                            7 80.8% 15% 4% 0.2%                                                            8 78.8% 15% 6% 0.2%                                                            9 75.8% 20% 4% 0.2%                                                            10 73.8% 20% 6% 0.2%                                                           11 71.8% 20% 8% 0.2%                                                                   JEFFAMINE ® ED-2003                                              12     80.8%    15%       4%        0.2%                                         13 78.8% 15% 6% 0.2%                                                           14 75.8% 20% 4% 0.2%                                                           15 73.8% 20% 6% 0.2%                                                           16 71.8% 20% 8% 0.2%                                                         ______________________________________                                    

                                      TABLE 29B                                    __________________________________________________________________________                  1  2  3   4  5  6  7  8  9  10 11 12 13  14 15 16                 __________________________________________________________________________     Flexural Modulus, MPa                                                                       208                                                                               290                                                                               368 417                                                                               273                                                                               251                                                                               282                                                                               272                                                                               329                                                                               310                                                                               313                                                                               263                                                                               227 292                                                                               295                                                                               280                  Stress at Yield, MPa 7.3 9.5 11.5 12.6 9.0 8.6 9.3 8.9 10.4 9.8 9.9 8.9                                                                  8.1 9.5 9.9                                                                    9.7                  Tensile Elongation, % 666 666 658 545 666 666 666 663 561 580 379 666                                                                    666 666 666                                                                    666                  Tensile Strength, MPa 12.3 12.9 12.7 11.6 11.7 11.5 12.3 11.5 11.1 10.6                                                                  9.8 11.8 12.2                                                                  11.8 11.3                                                                      11.4                 Hardness, Shore D 41 46 49 51 44 43 45 44 47 46 47 46 44 46 47 46                                                                         Notched Izod                                                                  Impact, J/m                                                                    353 400 438                                                                    393 378 381                                                                    379 403 250                                                                    321 150 404                                                                    378 423 373                                                                    380                  -30° C., J/m 655 153 46 24 70 12 71 48 15 25 23 44 58 24 24 27                                                                     Maximum                                                                       Load, J/m 973                                                                  906 961 966                                                                    895 889 894                                                                    832 881 854                                                                    850 906 922                                                                    921 895 935                                                                     -30°                                                                   C., J/m 1741                                                                   1658 1817                                                                      1538 1857                                                                      1731 1909                                                                      1865 854 1100                                                                  796 2068 1662                                                                  689 387 574                                                                     Total                                                                         Energy, J                                                                      21.0 21.0                                                                      20.2 17.5                                                                      19.8 19.2                                                                      19.0 17.7                                                                      15.8 16.6                                                                      15.3 19.3                                                                      18.9 18.5                                                                      15.4 19.1                                                                       -30°                                                                   C. 26.6 28.3                                                                   20.2 7.4 23.8                                                                  21.1 21.1                                                                      13.9 4.4 5.1                                                                   4.0 15.0 7.4                                                                   2.1 2.5 1.3                                                                     Ductile/5 5                                                                   5 5 5 5 5 5 5                                                                  5 5 5 5 5 5 5                                                                  5                    -30° C. 5 5 4 0 4 4 5 0 0 0 0 0 0 0 0 0                                 MFI, gm/10 min. 0.6 0.8 8.1 14 4.3 19  44 74 111 95 11 0.9 24 19 3.8                                                                      Paint                                                                         Adhesion                                                                       w/IPA, % 4 0                                                                   14 4 16 35 14                                                                  72 80 98 96 2                                                                  1 32 92 70                                                                      w/o IPA, % 1                                                                  1 20 8 14 16                                                                   6 78 98 92 92                                                                  10 1 36 91         __________________________________________________________________________                                                                 62            

Examples 28-29 demonstrate the improved properties of TPV-based compositions that have been modified with the reaction product of maleated PP and polyether amines, providing composition that are directly paintable. This paintability is surprising and unexpected in that TPV's used to make automotive parts, are not directly readily paintable to a commercially acceptable level. Instead, TPV-based compositions had to be treated, as described above for TPO-based compositions.

TPV-based compositions prepared in accordance with the practice of this invention generally may be directly painted, with or without primer, such that the paint adhesion is greater than about 75 percent based on the testing procedure used for Examples 28-29, preferably greater than about 85 percent, more preferably greater than about 90 percent, and most preferably greater than about 95 percent.

Performance improvements can be gained by incorporating polyetheramines into polyolefins such as polypropylene, polyethylene and copolymers of ethylene, propylene, alpha-olefins, and mixtures thereof, as well as polyolefins containing conjugated and unconjugated dienes, for textile and nonwoven applications. Polyetheramines can be incorporated into polyolefins by reacting the polyetheramine with a functionalized polyolefin. One example of such technology is the reaction of polyetheramine with maleated polypropylene in the presence of polypropylene. Such a reaction can be completed in an extruder or similar thermoplastic mixing device. An adduct of the reaction product of the maleated polypropylene/polyether amine can be produced in a reactor and then subsequently added to polypropylene or polyolefin for further processing.

The incorporation of polyetheramines into polyolefins will improve the dyeability of the polyolefin. The polar polyether segment is a site for the complexation of polar solvent or water based dyes. Typical polar dyes are not compatible with nonpolar polyolefins and would quickly bleed out of the fiber or filament.

The polyetheramines will improve the washability of a polyolefin based textile fabric or nonwoven mat. The nonpolar polyolefin tends to hold on to dirt due to the hydrophobic nature of both. The polyetheramine will allow detergents to penetrate the fabric or matrix so the detergents can loosen and wash away the dirt and oils.

The incorporation of polyether amines will increase the adsorption and wickability of polyolefin textiles and nonwovens. One example is the melt blown, nonwoven absorbent in baby diapers. Making the surface of the nonwoven filament more hydrophilic by incorporating the polar polyetheramine into the polyolefin will greatly increase the diaper's moisture absorption characteristics.

Suitable thermoplastic resin compositions useful in the manufacture of fibers and nonwovens should contain an effective amount of polyetheramine. In one embodiment of the present invention, the thermoplastic resin composition may contain up to about 12 wt % polyetheramine and up to about 30 wt % maleated polypropylene. In particular, the thermoplastic resin composition may contain up to 8 wt % polyetheramine and up to 20 wt % maleated polypropylene. In a preferred embodiment, the thermoplastic resin composition may contain from about 0.1 to about 5 wt % polyetheramine and from about 0.2 to about 15 wt % maleated polypropylene. In an especially preferred embodiment, the thermoplastic resin composition may contain from about 1 to about 4 wt % polyetheramine and from about 2 to about 12 wt % maleated polypropylene.

Applications of the fibers and filmanets from the polyether modified polyolefins include, with limitation: woven garments (outerwear and underwear); carpet; furniture and automobile upholstery; nonwoven absorbents used in diapers, sanitary pads, incontinence pads, spill abatement, and medical absorbent pads; nonwoven garments, including disposable medical garments; felts; pressed sheets; geo-textiles; filters (bipolar); and packaging materials, including envelopes.

EXAMPLES 30-45

In Examples 30-45, polyolefins, maleated polypropylene, and polyetheramine are compounded to produce a polyolefin blend that is used to produce polyolefin fibers having improved and unexpected results. Table 1 shows the amount and type of poleolefin and the amounts of poletheramine and maleated polypropylene which is compounded:

                  TABLE 1                                                          ______________________________________                                                Polyolefin                                                                               Polyolefin                                                                               Polyetheramine                                                                           Maleated                                    Run Type wt % wt % PP wt %                                                   ______________________________________                                         1      PP        98.7      0.5       0.8                                         2 PP 97.5 1 1.5                                                                3 PP 96.2 1.5 2.3                                                              4 PP 95 2 3                                                                    5 PP 93.7 2.5 3.8                                                              6 PP 92.5 3 4.5                                                                7 PP 91.2 3.5 5.3                                                              8 PP 90 4 6                                                                    9 PP 88.7 4.5 6.8                                                              10 PP 87.5 5 7.5                                                               11 PP 85 6 9                                                                   12 PP 82.5 7 10.5                                                              13 PP 80 8 12                                                                  14 PE 98.7 0.5 0.8                                                             15 PE 97.5 1 1.5                                                               16 PE 96.2 1.5 2.3                                                             17 PE 95 2 3                                                                   18 PE 93.7 2.5 3.8                                                             19 PE 92.5 3 4.5                                                               20 PE 91.2 3.5 5.3                                                             21 PE 90 4 6                                                                   22 PE 88.7 4.5 6.8                                                             23 PE 87.5 5 7.5                                                               24 PE 85 6 9                                                                   25 PE 82.5 7 10.5                                                              26 PE 80 8 12                                                                ______________________________________                                    

GLOSSARY

JEFFAMINE M-1000 ##STR6## JEFFAMINE M-2070 and JEFFAMINE M-2005 ##STR7## where R=H or CH₃, m is from about 3 to 32, and n is from about 10 to 32.

JEFFAMINE D-2000. JEFFAMINE D-4000 and JEFFAMINE D-400 ##STR8## where x is about 33 for D-2000, x is about 68 for D4000 and x is about 5.6 for D400. JEFFAMINE ED-600. JEFFAMINE ED-900. JEFFAMINE ED-2001. JEFFAMINE ED-4000, and JEFFAMINE ED-6000 ##STR9## where b is about 8.5 and a+c is about 2.5 for ED-600, b is about 15.5 and a+c is about 2.5 for ED-900, b is about 40.5 and a+c is about 2.5 for ED-2001, b is about 86.0 and a+c is about 2.5 for ED4000, and b is about 132.0 and a+c is about 3.0 for ED-6000.

JEFFAMINE T-3000 and JEFFAMINE T-5000 ##STR10## where x+y+z=50 for T-3000 and x+y+z=83 for T-5000. JEFFAMINE ET-3000 ##STR11## where x+y+z=57 and a+b+c=4. 

We claim:
 1. A composition comprising polypropylene, a polyolefin vulcanizate, and the reaction product of a functionalized polypropylene and a polyether amine.
 2. The compound of claim 1, wherein the functionalized polypropylene is derived from the free radical reaction of polypropylene and an olefinically unsaturated carboxylic acid.
 3. The compound of claim 2 wherein the olefinically unsaturated carboxylic acid is a monocarboxylic acid derived from acrylic acid or methacrylic acid, and the corresponding esters.
 4. The compound of claim 2 wherein the olefinically unsaturated carboxylic acid is a dicarboxylic acid derived from fumaric acid, maleic acid, and itaconic acid.
 5. The compound of claim 1 wherein the functionalized polypropylene is derived from the reaction of polypropylene and mono- and/or di- esters of olefinically unsaturated dicarboxylic acids wherein the olefinically unsaturated dicarboxylic acids are derived from mono-fumarate, di-fumarate, mono-maleate, or di-maleate.
 6. The compound of claim 1 wherein the functionalized polypropylene is derived from the reaction of polypropylene and an olefinically unsaturated carboxylic anhydride.
 7. The compound of claim 1 wherein the functionalized polypropylene is derived from the reaction of polypropylene and sulfo- or sulfonyl-containing olefinically unsaturated monomers wherein the olefinically unsaturated monomers are derived from p-styrenesulfonic acid, 2-(meth)acrylamide-2-methylpropenesulfonic acid or 2-sulfonyl-(meth)acrylate.
 8. The compound of claim 1 wherein the functionalized polypropylene is derived from the reaction of polypropylene and oxazolinyl-containing olefinically unsaturated monomers comprising vinyloxazolines and vinyloxazoline derivatives.
 9. The compound of claim 1 wherein the functionalized polypropylene is derived from the reaction of polypropylene and epoxy-containing olefinically unsaturated monomers, selected from the group consisting of glycidyl (meth)acrylate and allyl glycidyl ether.
 10. The compound of claim 1 wherein the polyether amine is selected from the group consisting of monoamines, diamines and triamines and has a molecular weight of from about 148 to 12,000.
 11. The composition according to claim 10, wherein the polyetheramine is a monoamine or diamine and having a molecular weight of from about 150 to about 12,000.
 12. The composition according to claim 1, wherein the polyetheramine is prepared from ethylene oxide and propylene oxide with the amount of ethylene oxide in the polyetheramine being greater than about 50 percent.
 13. The composition according to claim 1, wherein the composition comprises from about 5 to about 40 weight percent functionalized polypropylene, from about 2 to about 10 weight percent of polyether amine, and 50 to about 93 weight percent of polypropylene and elastomer.
 14. A composition useful as a material for making paintable automotive body parts, comprising:polypropylene; polyolefin vulcanizate; and the reaction product of maleated polypropylene and a polyether amine.
 15. The compound of claim 14 wherein the reaction product of maleated polypropylene and the polyether amine has the formula: ##STR12## wherein a is from about 5 to 50,000, for b:c from about 0:100 to 100:0, x is from about 1 to 3, and R is an alkyl moiety.
 16. The compound of claim 14 wherein the maleated polypropylene is selected from the group consisting of the structures having the formulae wherein PP is polypropylene: ##STR13##
 17. The compound of claim 14 wherein the polyether is selected from the group consisting of polyethylene glycol, polypropylene glycol and copolymers of polyethylene glycol and polypropylene glycol.
 18. The compound of claim 14 wherein the polyetheramine has the following structure: ##STR14## where R=H, CH₃, m is from about 3 to 32, and n is from about 10 to
 32. 19. The compound of claim 14 wherein the polyetheramine has the following structures: ##STR15## where b is about 40.5 and a+c is about 2.5, b is about 86.0 and a+c is about 2.5, and b is about 132.0 and a+c is about 2 to
 10. 20. The compound of claim 14 wherein the polyetheramine has the following formula: ##STR16##
 21. The compound of claim 14 wherein the polyether amine is selected from the group consisting of monoamines, diamines and triamines and has a molecular weight of from about 148 to 12,000.
 22. The compound of claim 21 wherein the polyether amine is a monoamine selected from the group having a molecular weight from about 200 to
 4000. 23. The compound of claim 22 wherein the monoamine has the following structure: ##STR17##
 24. The compound of claim 22 wherein the monoamine has the following structure: ##STR18## where R=H or CH, m is from about 3 to 32, and n is from about 10 to
 32. 25. The compound of claim 21 wherein the polyether amine is a diamine selected from the group having a molecular weight of from about 148 to
 6000. 26. The compound of claim 25 wherein the diamine is selected from the group consisting of compounds of the following structure: ##STR19## where b is about 8.5 and a+c is about 2.5, b is about 15.5 and a+c is about 2.5, b is about 40.5 and a+c is about 2.5, b is about 86.0 and a+c is about 2.5, and b is about 132.0 and a+c is about 2to
 10. 27. The compound of claim 21 wherein the diamine is selected from the group consisting of compounds of the following structure: ##STR20## where x is about 33, x is about 68, and x is about 5.6.
 28. The compound of claim 21 wherein the polyether amine is a triamine having the molecular weight of from about 200 to
 4000. 29. The compound of claim 28 wherein the triamine is selected from the group consisting of compounds having the following structure: ##STR21## where x+y+z=50 and x+y+z=83.
 30. The compound of claim 28 wherein the triamine has the following structure: ##STR22## where x+y+z=57 and a+b+c=3 to
 15. 31. The composition according to claim 14, wherein the maleated polypropylene has a number average molecular weight of about 3,000 to about 20,000.
 32. The composition according to claim 14, wherein the polyetheramine has a molecular weight in the range from about 1,500 to about 2,000 and is a monoamine or a diamine.
 33. The composition according to claim 14, wherein the polyetheramine is prepared from ethylene oxide and propylene oxide with the amount of ethylene oxide in the polyetheramine being greater than about 50 percent.
 34. The composition according to claim 32, wherein the polyetheramine is a monoamine and wherein the polyetheramine is prepared from ethylene oxide and propylene oxide wherein the amount of ethylene oxide in the polyetheramine on a molar basis is greater than about 75 percent.
 35. The composition according to claim 34, wherein the amount of ethylene oxide is greater than about 90 percent.
 36. The composition according to claim 14, wherein the maleated polypropylene has a number average molecular weight of from about 3,000 to about 20,000.
 37. The composition according to claim 14, wherein the composition comprises maleated polypropylene in an amount in the range from about 5 to about 40 weight percent and polyetheramine in an amount in the range from about 2 to about 10 weight percent.
 38. The composition according to claim 14, wherein the polyetheramine is a monoamine or diamine having a molecular weight in the range from about 1,000 to about 3,000 and wherein the polyetheramine is prepared from propylene oxide, ethylene oxide or combination thereof.
 39. The composition according to claim 14, wherein the polyetheramine is prepared from ethylene oxide, propylene oxide or combination thereof.
 40. The composition according to claim 14, in the absence of an amine other than a polyetheramine and in the absence of a copolymer of an olefin and maleic anhydride.
 41. The composition according to claim 14, wherein the paint adhesion of the composition is greater than 95 percent.
 42. The composition according to claim 14, further comprising a glass filler in an amount up to about 40 weight percent.
 43. A process for preparing a composition useful for making molded automotive body parts, comprising: feeding polypropylene, crosslinked thermoplastic polyolefin, maleated polypropylene, and polyether amine to a mixing apparatus at a temperature in the range from about 175° C. to about 300° C. under conditions such that a reaction product of the maleated polypropylene and the polyether amine is formed.
 44. The process of claim 43 wherein the reaction product of maleated polypropylene and the polyether amine has the formula: ##STR23## wherein a is from about 5 to 50,000, for b:c from about 0:100 to 100:0, x is from about 1 to 3, and R is an alkyl moiety.
 45. The process of claim 43 wherein the maleated polypropylene is selected from the group consisting of the structures having the formulae wherein PP is polypropylene: ##STR24##
 46. The process of claim 43 wherein the polyether is selected from the group consisting of polyethylene glycol, polypropylene glycol and copolymers of polyethylene glycol and polypropylene glycol.
 47. The process of claim 43 wherein the polyetheramine has the following structure: ##STR25## where R=H, CH₃, m is from about 3 to 32, and n is from about 10 to
 32. 48. The process of claim 43 wherein the polyetheramine has the following structures: ##STR26## where b is about 40.5 and a+c is about 2.5, b is about 86.0 and a+c is about 2.5, and b is about 132.0 and a+c is about 2 to
 10. 49. The process of claim 43 wherein the polyetheramine has the following formula: ##STR27##
 50. The process of claim 43 wherein the polyether amine is selected from the group consisting of monoamines, diamines and triamines and has a molecular weight of from about 148 to 12,000.
 51. The process of claim 50 wherein the polyether amine is a monoamine selected from the group having a molecular weight from about 200 to
 4000. 52. The process of claim 51 wherein the monoamine has the following structure: ##STR28##
 53. The process of claim 51 wherein the monoamine has the following structure: ##STR29## where R=H or CH, m is from about 3 to 32, and n is from about 10 to
 32. 54. The process of claim 50 wherein the polyether amine is a diamine selected from the group having a molecular weight of from about 148 to
 6000. 55. The process of claim 54 wherein the diamine is selected from the group consisting of compounds of the following structure: ##STR30## where b is about 8.5 and a+c is about 2.5, b is about 15.5 and a+c is about 2.5, b is about 40.5 and a+c is about 2.5, b is about 86.0 and a+c is about 2.5, and b is about 132.0 and a+c is about 2 to
 10. 56. The process of claim 50 wherein the diamine is selected from the group consisting of compounds of the following structure: ##STR31## where x is about 33, x is about 68, and x is about 5.6.
 57. The process of claim 50 wherein the polyether amine is a triamine having the molecular weight of from about 200 to
 4000. 58. The process of claim 57 wherein the triamine is selected from the group consisting of compounds having the following structure: ##STR32## where x+y+z=50 and x+y+z=83.
 59. The process of claim 57 wherein the triamine has the following structure: ##STR33## where x+y+z=57 and a+b+c=3 to
 15. 60. The process according to claim 43, wherein the maleated polypropylene has a number average molecular weight of about 3,000 to about 20,000.
 61. The process according to claim 43, wherein the polyetheramine has a molecular weight in the range from about 1,500 to about 2,000 and is a monoamine or a diamine.
 62. The process according to claim 43, wherein the polyetheramine is prepared from ethylene oxide and propylene oxide with the amount of ethylene oxide in the polyetheramine being greater than about 50 percent.
 63. The process according to claim 61, wherein the polyetheramine is a monoamine and wherein the polyetheramine is prepared from ethylene oxide and propylene oxide wherein the amount of ethylene oxide in the polyetheramine on a molar basis is greater than about 75 percent.
 64. The process according to claim 63, wherein the amount of ethylene oxide is greater than about 90 percent.
 65. The process according to claim 43, wherein the maleated polypropylene has a number average molecular weight of from about 3,000 to about 20,000.
 66. The process according to claim 43, wherein the composition comprises maleated polypropylene in an amount in the range from about 5 to about 40 weight percent and polyetheramine in an amount in the range from about 2 to about 10 weight percent.
 67. The process according to claim 43, wherein the polyetheramine is a monoamine or diamine having a molecular weight in the range from about 1,000 to about 3,000 and wherein the polyetheramine is prepared from propylene oxide, ethylene oxide or combination thereof.
 68. The process according to claim 43, wherein the polyetheramine is prepared from ethylene oxide, propylene oxide or combination thereof.
 69. The process according to claim 43, in the absence of an amine other than a polyetheramine and in the absence of a copolymer of an olefin and maleic anhydride.
 70. The process according to claim 43, wherein the paint adhesion of the composition is greater than 95 percent.
 71. The process according to claim 43, further comprising a glass filler in an amount up to about 40 weight percent.
 72. The process of claim 43, further comprising preparing a molded automotive body part by injection molding a blend made in accordance with the feeding step; and painting the molded automotive body part.
 73. An article of manufacture made in accordance with claim
 72. 